在等效应变幅为0.22%时,研究了Al-7Si-0.3Mg铸造铝合金在比例、圆形.正方形,菱形,矩形与椭圆形路径下的循环变形行为,并用TEM观察了疲劳失效试样的位错结构.结果表明:在多轴加载条件下,材料均表现出循环硬化现象,循环硬化的速率和程度对加载路径有依赖性;非比例载荷下材料的疲劳寿命远小于比例加载时的寿命,且非比例加载下的疲劳寿命对各种非比例加载路径有依赖性,其中圆形路径下疲劳寿命最短;位错在不同的加载路径下形成不同的组态结构,位错与强化相、枝晶界及位错问的交互作用是铸造铝合金发生循环硬化的主要原因.

Widely application of cast aluminum alloy requires an understanding of its cyclicdeformation behavior which is material dependent,and it is a complex function of strain amplitude,loading path,etc.In this study,multi-axial fatigue tests were conducted on cast Al-7Si-0.3Mg alloy with the same equivalent strain amplitude of 0.22%under six multi-aXial path loadings,whjch were proportional,circular,square,diamond,rectangle and ellipse paths.TEM was employed to investigate the dislocation structures of the fatigue failure specimens.Cyclic hardening dominates the whole fatigueprocess under every loading path,but the rate and extent of cyclic hardening are quite dependent on particular loading paths.The fatigue life under nonproportional loading is much lower than that under proportional loading,and it also depends on the various nonproportional loading paths.The specimen with circular path loading has the shortest life and the most severe cyclic hardening among all the loading paths.The continuously changing of direction of maximum shear-stress plane is attributedto the complicated dislocation substructures and severe stress concentration during the cyclic process-The interaction among dislocation,particle and cell boundary is the main reason for cyclic hardening.The structure and density of dislocation in fatigue failure specimens under various loading paths exhibit quite different.From double dislocation bands,multiple dislocation bands,labyrinth structure to cell structure.the dislocation mobility decreases and stress concentration degree increases.KEY WoRDS Al-7Si-0.3Mg alloy,nonproportional loading,multi-axial fatigue,dislocation

参考文献

[1] Miller W S,Zhuang L,Bottema J,Wittebrood A J,De Smet P,Haszler A,Vieregge A.Mater Sci Eng,2000;A280:37
[2] Wang M J,Huang D Y,Jiang H T.Heat Treat Met,2006;31(9):34(王孟君,黄电源,姜海涛.金属热处理,2006;31(9):34)
[3] Ding X Q,He G Q,Chen C S,Liu X S,Zhu Z Y.J MaterSci Eng,2005;23:302(丁向群,何国球,陈成澍,刘小山,朱正宇.材料科学与工程学报,2005;23:302)
[4] Wang Q G,ApeUan D,Lados D A.J Light Met,2001;1:73
[5] Wang Q G,Apelian D,Lados D A.J Light Met,2001;1:85
[6] McDowell D L,Gall K,Horstemeyer M F,Fan J.Eng Fract Mech,2003;70:49
[7] Mo D F,He G Q,Hu Z F,Zhu Z Y,Chen C S,Zhang W H.Int J Fatigue.2008;30:1843
[8] Kida S,Itoh T,Sakane M,Ohnami M,Socie D F.Fatigue Fract Eng Mater Siruct.1997;20:1375
[9] He G Q,Chen C S,Gao Q.Acta Metall Sin,2003;39:715(何国求,陈成澍,高庆.金属学报,2003;39:715)
[10] Wang S Z.Fatigue of Metal.Beijing:Science and Tech-nology Press,1985:528(王栓柱.金属疲劳.北京:科学技术出版社,1985:528)
[11] Suresh S,translated by Wang Z G,et al.Fatigue of Mate-rials.2nd Ed.,Beijing:National Defence Industry Press,1999:190(Suresh S著;王中光等译.材料的疲劳.第2版,北京:国防工业出版社,1999:190)
[12] Wang Q G.Metall Mater Trans,2004;35A:2707
[13] Nie J F,Muddle B C,Aaronson H I,Ringer S P,High JP Metall Mater Trans,2002;33A:1649
[14] Chakrabarti D J,Laughlin D E.Prog Mater Sci 2004,49:389
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%