用电弧离子镀方法在质子交换膜燃料电池(PEMFC)不锈钢双极板表面沉积一系列Cr1-xNx(x=0.28-0.50)改性薄膜,对薄膜的成分、相组成以及改性双极板的导电、耐蚀等性能进行了分析测试.结果表明,双极板的导电与耐蚀性能因沉积Cr1-xNx薄膜而显著提高,并且与薄膜的成分和相组成密切相关:当x值从0.28增加到0.50,薄膜由Cr+Cr2N转变为Cr2N,再转变为Cr2N+CrN,最终变为CrN;当薄膜由单相组成时,双极板既导电又耐蚀、综合性能最好,与原始不锈钢相比,导电性能提高2个数量级以上,而耐蚀性能提高近3个数量级.
参考文献
| [1] | Keith B P.J Power Sources,1994; 51:129 |
| [2] | Wind J,Spah R,Kaiser W,BShm G.J Power Sources,2002; 105:256 |
| [3] | Kelly M J,Fafilek G,Besenhard J O,Kronberger H,Nauer G E.J Power Sources,2005; 145:249 |
| [4] | Brady M P,Weisbrod K,Paulauskas I,Buchanan R A,More K L,Wang H,Wilson M,Garzon F,Walker L R.Scr Mater,2004; 50:1017 |
| [5] | Paulauskas I E,Brady M P,Meyer Ⅲ H M,Buchanan R A,Walker L R.Corros Sci,2006; 48:3157 |
| [6] | Wang H,Brady M P,Teeter G,Turner J A.J Power Sources,2004; 138:86 |
| [7] | Wang H,Brady M P,More K L,Meyer Ⅲ H M,Turner J A.J Power Sources,2004; 138:79 |
| [8] | Brady M P,Wang H,Yang B,Turner J A,Bordignon M,Molins R,Elhamid M A,Lipp L,Walker L R.Int J Hydrogen Energy,2007; 32:3778 |
| [9] | Fu Y,Hou M,Lin G Q,Hou J B,Shao Z G,Yi B L.J Power Sources,2008; 176:282 |
| [10] | Fu Y,Lin G Q,Hou M,Wu B,Li H K,Hao L X,Shao Z G,Yi B L.Int J Hydrogen Energy,2009; 34:453 |
| [11] | Wu B,Wang W T,Zhang M,Fu Y,Lin G Q.Chin J Power Source,2007; 31:861(吴博,王文涛,张敏,付宇,林国强.电源技术,2007;31:861) |
| [12] | Fu Y,Hou M,Lin G Q,Shao Z G,Yi B L.J Xi'an Jiao Tong Univ,2008; 42:364(付宇,侯明,林国强,邵志刚,衣宝廉.西安交通大学学报,2008;42:364) |
| [13] | Wang H L,Sweikaxt M A,Turner J A.J Power Sources,2003; 115:243 |
| [14] | Aouadi S M,Schultze D M,Rohde S L,Wong K G,Mitchell K A R.Surf Coat Technol,2001; 140:269 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%