在恒定磁场作用下对Al-Pb合金进行了快速定向凝固实验,考察了磁场强度对凝固组织的影响,分析了磁场的作用机理.结果表明,恒定磁场能显著减弱熔体对流,提高凝固界面前沿液-液相变过程的空间均匀性,减缓液滴的碰撞凝并速度,使凝固试样中的弥散相粒子最大和平均尺寸减小,粒子尺寸分析布范围变窄,有助于获得弥散型偏晶合金凝固组织.
The effect of a static magnetic field on the solidification of monotectic alloy has attracted great attentions. But up to date little is known about the details of the magnetic field influences on the microstructure development during the solidification of a monotectic alloy. In this paper, rapid directional solidification experiments are carried out with Al-Pb alloys under a static magnetic field. The dependence of the solidification microstructure on the intensity of the magnetic field is investigated. The mechanism through which the magnetic field affects the microstructure forlnation is analyzed. It is indicated that the static magnetic field cruises only a small decrease in the Marangoni migration velocity and the Stokes settlement velocity of the minority phase droplets during the liquid-liquid decomposition. Such a small change in the moving velocity of the droplets has only a negligible effect on the microstructure formation. The static magnetic field can suppress the convection efficiently. It enhances the spatial homogeneity of the liquid-liquid phase transformation along the radial direction of the sample, reduccs the collision and coagulation frequency betwecn the minority phase droplets and, therefore, causes a decrease in the largest and average sizes of the Pb-rich particles in the solidified sample as well as in the width of the particles size distribution. A static magnetic field is favorable for obtaining a inonotectic alloy with well dispersed microstructure.
参考文献
| [1] | Zhao J Z,Ratke L.Z Metallkd,1998; 89:241 |
| [2] | Zhao J Z,Ratke L.Scr Mater,1998; 39:181 |
| [3] | Liu Y,Guo J J,Jia J,Su Y Q,Ding H S.Acta Metall Sin,2001; 9:917(刘源,郭景杰,贾均,苏彦庆,丁宏升.金属学报,2001;9:917) |
| [4] | Wang N,Wei B B.Mater Sci Eng,2003; A345:145 |
| [5] | Zhao J Z.Acta Metall Sin,2002; 38:525(赵九洲.金属学报,2002;38:525) |
| [6] | Zhao J Z,Ratke L,Jia J,Li Q C.J Mater Sci Technol,2002; 18:197 |
| [7] | Guo J J,Cui H B,Su Y Q,Bi W S,Jia J,Fu H Z.Spec Cast Nonferrous Alloys,2004; 1:1(郭景杰,崔红保,苏彦庆,毕维生,贾均,傅恒志.特种铸造及有色合金,2004;1:1) |
| [8] | Decarlo J L,Pirch R G.Metall Trans,1984; 15A:2155 |
| [9] | Foner S,Meniff E.Rev Sci Instr,1968; 139:171 |
| [10] | He J,Zhao J Z,Li H L,Zhang X F,Zhang Q X.Metall Mater Trans,2008; 39A:1174 |
| [11] | Zhang L,Wang E G,Zuo X W,He J C.Acta Metall Sin,2008; 44:165(张林,王恩刚,左小伟,赫冀成,金属学报,2008;44:165) |
| [12] | Yasuda H,Ohnaka I,Fujimoto S.Mater Lett,2004; 58:911 |
| [13] | Yzsuda H,Ohnaka I,Fujimoto S.Scr Mater,2006; 54:527 |
| [14] | Chester W.J Fluid Mech,1957; 3:304 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%