研究了改变溶液的酸碱度来控制TiCl4水解,制备锐钛矿相超细TiO2纳米粉体的过程.采用XRD、TEM、SAED和TG-DTA等方法对所得粉体进行了表征,发现水解后的沉淀经真空干燥后,不用任何热处理,室温下即有锐钛矿相存在,其原始粒径约为3.8nm,粉体于400℃煅烧2h,可得到平均粒径为7nm的纯锐钛矿相纳米氧化钛粉体.