本文介绍用化学共沉淀和在适当温度下煅烧以直接制备YAG-Al2 O3纳米复合粉体的新方法．XRD结果表明，所得粉体具纯的YAG和α-Al2 O3相，因此其化学组成符合配料的组分设计．用本方法制备的25vol％YAG-Al2 O3复合粉体经热压烧结，所得的致密体材料为晶内型纳米复合材料，其抗弯强度达612MPa，断裂韧性为4．54MPa．m-1/2，都比单相Al2 O 3陶瓷有大幅度提高．
25vol%YAG-Al2 O3 nanocomposite powders were prepared by the co-precipitaion method from ytrium nitrate and aluminium nitrate as starting materials. The XRD pattern for the prepared powder calcined at 1300 ℃ for 1h shows well-defined peaks whose positions are almost identical to those of stoichometic YAG and α-Al2 O3. The powder compacts by hot-press sintering for 0.5 h at 1400 ℃ and 300MPa reached a density close to the thoretical, while the normally reported hot-press sintering temperature for YAG-Al2 O3 composites is 1600 ℃. The bending strength and fracture toughness of prepared 25vol%YAG-Al2 O3 nanocomposite were 612 MPa and 4.54 MPa.m-1/2, respectively, which are much higher than those of monolithic A l2 O3 and monolithic YAG, as well as higher than those reported in other studies for YAG-A l2 O3 composites.Microstructure studies found that the nano-YAG particles were mainly located within the Al2 O3grains.
参考文献
| [1] | Parthasarathy T A, Mah T, Keller K. J. Amer. Ceram. Soc., 1992, 75: 1756-1759. |
| [2] | Corman G S. Ceram Eng. Sci. Proc., 1991, 12: 1745-1766. |
| [3] | Matson L E, Hay R S, Mah T. Ceram. Eng. Sci. Proc., 1990, 11: 995-1003. |
| [4] | Gao L, Wang H Z, Hong J S, et al. J. Euro. Ceram. Soc., 1999, 19: 609-613. |
| [5] | Wang H Z, Gao L, Gui L H, et al. Nanostructured Materials, 1998 10: 947-953. |
| [6] | Warshaw I, Roy R. J. Amer. Ceram. Soc., 1959, 42: 434-438. |
| [7] | Viechnicki D, Caslavsky J. Amer. Ceram. Soc. Bull., 1979, 58: 790-791. |
| [8] | Gao L, Shen Z J, Miyamoto H, et al. J. Amer. Ceram. Soc., 1999, 82: 1061-1063. |
| [9] | Niihara K. J. Ceram Soc. Jpn., 1991, 99: 974-982. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%