考察了等离子喷涂Cr3C2-NiCr涂层及其表面化学镀Ni镀层通过不同配副组成摩擦副的摩擦学特性，并应用SEM、XRD和XPS对磨痕进行了分析. 结果发现：等离子喷涂Cr3C2-NiCr涂层及其表面化学镀Ni镀层自配副组成摩擦副，均表现出较大的摩擦系数和磨损系数；但是，Cr3C2-NiCr涂层表面化学镀Ni镀层与Cr3C2-NiCr涂层配副组成摩擦副，在干摩擦条件下，能达到0.12的摩擦系数和接近10-6mm3(Nm)-1的磨损系数. 上述结果是由于Cr3C2-NiCr涂层的磨损机理从强烈的层状颗粒剥落转变为沿气孔和微裂纹等处的颗粒断裂.
Tribological properties of plasma-sprayed Cr3C2-NiCr coatings without or with electroless plated Ni were investigated, and the worn surfaces were analyzed by employing SEM, XRD and XPS. It was found that both the self-mated rubbing pairs consisting of the Cr3C2-NiCr coating and the Cr3C2-NiCr coating electroless plated with Ni displayed higher friction coefficient and wear coefficient. However, The rubbing pair of the Cr3C2-NiCr coating electroless plated with Ni against the Cr3C2-NiCr coating had a friction coefficient of 0.12 and a wear coefficient close to 10-6mm3(Nm)-1 even if under dry sliding. The improvement in tribological properties could be attributed to that the wear mechanism of Cr3C2-NiCr coating transformed to particle fracturing along pores and microcracks from the intensive spalling along splat interfaces.
参考文献
| [1] | Hirvonen J-P, Koskinen J, Jervis J R, et al. Surface and Coatings Technology, 1996, 80: 139-150. |
| [2] | Barbezat G, Moens J R, Nicoll A R. Materials & Design, 1992, 13 (3): 145-148. |
| [3] | Takeuchi J, Muratay Y, Haraday Y, et al. Proceedings of the 15th International Thermal Spray Conference. Nice, France, 1998. 1425-1430. |
| [4] | 金元生, 夏为民, 程华. 清华大学学报, 1992, 32 (5): 17-25. |
| [5] | Mohanty M, Smith R W, Bonte M D, et al. Wear, 1996, 198: 251-266. |
| [6] | Li J F, Ding C X, Huang J Q, et al. Wear, 1997, 211: 177-184. |
| [7] | Czichos H, Klaffke D, Santner E, et al. Wear, 1995, 190: 155-161. |
| [8] | Jin Y S, Li M Y, Wang Y. Wear, 1994, 172: 147-154. |
| [9] | Corte C D, Sliney H E. Tribological Transactions, 1995, 38 (4): 845-850. |
| [10] | Hajdu J. Plating & Surface Finishing, 1996, 83 (9): 29-33. |
| [11] | 余来贵, 张绪寿. 摩擦学学报,1992, 12 (2): 123-130. |
| [12] | Dennis J K, Sheikh S T, Silverstone E C. Transactions of the Institute of Metal Finishing, 1981, 59: 118-122. |
| [13] | 吴玉程, 黄录官, 邓宗钢, 等. 摩擦学学报, 1992, 12 (2): 144-152. |
| [14] | 刘颍, 陈家钊, 涂铭旌, 等. 摩擦学学报, 1998, 18 (1): 71-74. |
| [15] | Li J, Zhang Y, Huang J, et al. Journal of Thermal Spray Technology, 1998, 7 (2): 242-246. |
| [16] | 王世中, 臧鑫士. 现代材料研究方法. 北京：北京航空航天大学出版社. 1991. 259-260. |
| [17] | Su Y S, Lin J S. Wear, 1993, 166: 27-35. |
| [18] | Li C, Ohmori A, Mcpherson R. Journal of Materials Science, 1997, 32: 997-1004. |
| [19] | Smith R W, Novak R. Powder Metallurgy International, 1991, 23 (3): 147-152. |
| [20] | Ahn H S, Roylance B J. Tribology International, 1992, 25 (4): 227-236. |
| [21] | 迪安 A J. 兰氏化学手册[M]. 尚方久,操时杰,辛无名, 等译. 北京：科学出版社,1991. 4-12. |
| [22] | Wang Y, Jin Y, Wen S. Wear, 1988, 128: 277-290. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%