采用有机泡沫浸渍工艺制备了碳化硅基网眼多孔陶瓷.研究了真空脱气处理对浆料流变特性和烧结体的力学性能及显微结构的影响.结果表明:脱气处理改善了浆料的流变特性,使浆料在有机泡沫体上的涂覆量增加和结构均匀性得到改善;压汞仪测试数据和SEM观察表明脱气处理明显地消除了孔筋内的孔径为100μm左右的大气孔;经脱气处理后,材料的抗弯强度从2.34MPa提高到3.18MPa.脱气处理对网眼陶瓷强度的改善主要来自两方面的贡献:一是相对密度的增加,二是孔筋中大气孔的消除,但后者是最主要的贡献,这个结果与目前建立的开孔陶瓷泡沫的力学模型吻合得很好.
参考文献
| [1] | Saggio-Woyansky J, Scott C E, et al. Am. Ceram. Soc. Bull., 1992, 71 (11): 1674-1682. |
| [2] | Montanaro L, Jorand Y, Fantozzi G, et al. J. Euro. Ceram. Soc., 1998, 18: 1339-1350. |
| [3] | Hendricks T J, Howell J R. Journal of Heat Transfer. 1996, 115: 911-917. |
| [4] | Gibson L G, Ashby M F. Cellular Solids .. Structure and properties-second edition, CambridgeUniversity Press, 1997. |
| [5] | Brezby R, Green D J. Mechanical behavior of cellular ceramics. In Materials Science and Technology,Vol. 11, Structure and Properties of Ceramics. R. W. Cahn, P. Haasen and E. J. Kramer. VCH,Germany, 1992. 467-516. |
| [6] | Brown D D, Green D J. J. Am. Ceram. Soc., 1994, 77 (6): 1467-1472. |
| [7] | Reed J S. Principles of Ceramics Porcessing, Second Edtion, Copyright(c) 1995 by John & Sons, Inc. |
| [8] | 朱新文,江东亮.硅酸盐通报,2000,19(3):45-51. |
| [9] | 张兆泉.中国科学院上海硅酸盐研究所博士论文,2000年. |
| [10] | Orenstein R M, Green D J. J. Am. Ceram. Soc., 1992, 75 (7): 1899-1905. |
| [11] | Vedula V R, Green D J, Hellman J R. J. Am. Ceram. Soc., 1999, 82 (3): 649-656. |
| [12] | Rasto Brezny, David J. Green, J. Am. Ceram. Soc., 1989, 72 (7): 1145-1152. |
| [13] | 龚森蔚.中国科学院上海硅酸盐研究所硕士论文,1998年. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%