设计了部分化学法制备PbNb(Zr,Sn,Ti)O3反铁电陶瓷粉体.前驱体在600℃/2h的预烧条件下形成钙钛矿晶相结构,经行星球磨后获得亚微米级粒度分布的粉体.采用流延法成型,在1100℃/4h的烧结条件下获得了相对密度>97%,晶粒大小约为4μm的样品.在组成为Pbo 99Nbo 02[(Zro.6Sno.4)1-yTiy]0.98O3的系列样品中,随Ti含量增加,样品出现从反铁电态向铁电态转变的趋势.在y=0.06的配方中,在6kV/mm场强下测得了0.33%的纵向应变.
参考文献
| [1] | Berlincourt D.IEEE Trans.Sonic Ultrason.,1966,SU-13(4):116-125. |
| [2] | Thacher P D.Appl.Phys.,1968,39(4):1996-2002. |
| [3] | Berlincourt D,Jaffe H,Krueger H H,et al.J.Phys.Lett.,1971,3:501-505. |
| [4] | Berlincourt D,Krueger H H,Jaffe B.J.Phys.Chem.Solids,1964,25:659-674. |
| [5] | Uchino K,Nomura S.Ferroelectrics,1983,50:191-195. |
| [6] | Uchino K,Jpn.J.Appl.Phys.,1985,24,Suppl.24-2:460-468. |
| [7] | Yang P,Payne D A.Ceram.Trans.,1992,32:347-354. |
| [8] | Akiyama T,Fujisawa E.Jpn.J.Appl.Phys.,1997,36:5997-6000. |
| [9] | Uchino K.Piezoelectric Actuators and Ultrasonic Motors,Boston:Kluwer Academic Publisher.1997.320. |
| [10] | Smolensky G A,et al.Fiv.Tverdogo.Tela,1960,2:1906. |
| [11] | Harnderek J,Ujma Z.J.Phys:Condes.Matter.,1995,7:1721-1728. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%