以SnCl4.5H2O为主要原料,用溶剂热技术在油酸体系中成功地合成了具有精细结构的SnO2纳米球.X射线衍射(XRD)和选区电子衍射(SAED)结果表明,制备出的SnO2微晶具有良好的结晶性;透射电镜(TEM)结果表明,得到的产物中含有尺寸约为50～80nm的SnO2纳米球,放大的TEM照片进一步揭示了此纳米球含有粒度为2～6nm超细粒子的精细结构.这种结构趋向于高的比表面积,适合于气敏探测器方面的应用.
参考文献
| [1] | Daw A L, Johsi J C. J. Mater. Sci., 1984, 19: 1-4. |
| [2] | Chopra K L, Major S, Pandya D K. Thin Solid Films, 1983, 102: 1-5. |
| [3] | Vosson J L. Phys, Thin Films, 1997, 7: 1-4. |
| [4] | Lalauze R, Breuil P, Pijolat C. Sensors Actuators B, 1991, 3: 175-179. |
| [5] | Kane J, Scheweizer H P, Kern W. J. Electrochem. Soc., 1976, 123: 270-275. |
| [6] | Baliga B J, Gandhi S K. J. Electrochem. Soc., 1976, 123: 941-944. |
| [7] | Rohatgi A, Viverio T R, Slack L H. J. Am. Ceram. Soc., 1974, 57: 278-283. |
| [8] | Kim H, Laitinen H A. J. Am. Ceram. Soc., 1975, 58: 23-26. |
| [9] | Miki-Yoshida M, Andrade E. Thin Solid Films, 1993, 224: 87-92. |
| [10] | Watanabe H. J. Appl. Phys., 1970, 9: 1551-1554. |
| [11] | Carson D E. Electrochem. Soc., 1975, 122: 1334-1337. |
| [12] | Lahmann H W, Widmei R. Thin Solid Films, 1975, 27: 359-363. |
| [13] | Sidney J L Ribeiro, Sandra H Pulcinelli, Celso V Santilli, et al. Chem. Phys. Lett., 1992, 190:64-68. |
| [14] | Sung-Soon Park, Haixing Zhang, Mackenzie J D. Mater. Lett., 1993, 17: 346-350. |
| [15] | Ogawa H, Abe A, Nishikannaand N, et al. J. Electrochem. Soc., 1981, 128: 2020-2024. |
| [16] | Pisarkiewiez T, Stapinski T. Thin Solid Films, 1989, 174: 277-280. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%