以沉淀法制备的纳米TiO2/Cr2O3复合粉体为原料,采用氨解法在800℃、氮化8h制备了纳米Ti0.8Cr0.2OxNy粉体.对纳米TiO2/Cr2O3复合粉体和合成的氧氮化物粉体用俄歇电子能谱(AES)、氮吸附比表面积(BET)、X射线衍射(XRD)、透射电子显微镜(TEM)、电子探针显微分析(EPMA)等方法进行了表征.结果表明:沉淀法可以制备出组成均匀的纳米TiO2/Cr2O3复合粉体,该复合粉体在800℃氮化8h可得到粒度为20～30nm的纯立方相Ti0.8Cr0.2OxNy纳米粉体,其比表面积达46.74m2/g.
参考文献
| [1] | Grins J, Kall P O, Svensson G. J. Mater. Chem., 1995, 5 (5): 571-574. |
| [2] | Oyama S T. US patent 5444173, 1995. |
| [3] | Grins J. J. Europ Ceram Soc., 1997, 17: 1819-1824. |
| [4] | El-Himri A, Sapinna F, Ibannez R, et al. J. Mater. Chem., 2000, 10: 2537-2541. |
| [5] | Elder S H, Dasalvo F J, Parise J B. J. Solid State Chem., 1994, 108: 73-79. |
| [6] | Alconchel S, Sapinna F, Beltran D, et al. J Chem. Mater., 1999, 9: 749-755. |
| [7] | Lee K H, Park C H, Yoon Y S, et al. Thin Solid Films, 2001, 385: 167-173. |
| [8] | Vetter J, Scholl H J, Knotek O. Surf. Coat. Technol., 1995, 74/75: 286-291. |
| [9] | Hones P, Sanjinés R, Lévy F. Thin Solid Films, 1998, 332: 240-246. |
| [10] | Nainaparampil J J, Zabinski J S, Korenyi-Both A. Thin Solid Films, 1998, 333: 88-94. |
| [11] | Li J G, Gao L, Sun J, et al. J. Amer. Ceram. Soc., 2001, 84 (12), 3045-3047. |
| [12] | Li Y G, Gao L, Li J G, et al. J. Amer. Ceram. Soc., 2002, 85 (5): 1294-1296. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%