采用sol-gel方法制备了ZnFe2O4/Fe2O3纳米复相铁氧体.利用X射线衍射,高分辨电镜(HREM)对样品的结构进行了分析.结果表明,复相锌铁氧体是形成隧道结构的必要条件;伏安曲线和磁电阻效应等从性能上说明复相锌铁氧体具有隧道磁电阻的特性;HREM直接观测到复相锌铁氧体形成隧道结构,其中绝缘层α-Fe2O3位于晶界处,从相变动力学分析中,也证实了α-Fe2O3是由ZnFe2O4晶界或表面控制的析晶,位于晶界处.
参考文献
| [1] | Hunt R P. IEEE Trans. Magn., 1971, 7: 150-155. |
| [2] | Johnson M. Science, 1993, 260: 320-324. |
| [3] | Tsang C, Chen M M, Yogi T, et al. IEEE Trans. Magn., 1990, 26: 1689-1693. |
| [4] | Berkowitz A E. Phys. Rev. Lett., 1992, 68: 3745-3748. |
| [5] | Olhm A V. IEEE Trans, Magn., 1995, 31: 3200-3204. |
| [6] | Baibich M N. Phys. Rev. Lett., 1988, 61: 2472-2475. |
| [7] | John. G Xiao, Jiang J S, Chien C C. Phys. Rev. Lett., 1992, 68: 3749-3752. |
| [8] | Jin S. Science, 1994, 264: 413-417. |
| [9] | Miyazaki T, Tezuka N. J. Magn. Magn. Mater., 1995, 139: L231-234. |
| [10] | Moodera J S. Phys. Rev. Lett., 1995, 74: 3273-3276. |
| [11] | Fujimori H, Mitani S, Ohnuma S. Mater. Sci. Eng., 1995, B31: 219-221. |
| [12] | Moodera J S, Kinder L R. Phys. Rev. Lett., 1995, 74: 3273-3276. |
| [13] | Wang Z G, Nakamura Y. IEEE Mag., 1996, 32: 4022-4026. |
| [14] | chen P, Xing D Y, Du Y W. Phys. Rev. Lett., 2001, 87: 1-4. |
| [15] | 都有为,陈鹏,朱建民,等.物理学报,2001,50:2275-2280. |
| [16] | 冯端,等.金属物理学,第二版.北京:科学出版社,1998.180-190. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%