利用熔融法制备了BaO-SrO-TiO2-SiO2玻璃,并在温度梯度条件下制备了极性微晶Ba2-zSrxTiSi2O8沿c轴一维取向的压电玻璃陶瓷.用X-ray衍射分析和扫描电镜对极性微晶的取向生长结构进行了分析.建立了极性微晶沿c轴取向生长的模型,其结果与实验结果相一致.结果表明在光滑的表面,温度梯度方向和偶极子电场方向都是沿c轴晶格能大的方向,其共同作用的结果使极性微晶沿c轴一维取向生长.
参考文献
| [1] | Halliyal A, Bhalla A S, Newnham R E, et al, J. Mat. Sci, 1982, 17: 295-300. |
| [2] | Halliyal A, Bhalla A S, Markgray S A, et al, Ferroelectrics, 1985, 62: 27-38. |
| [3] | Halliyal A, Bhalla A S, Cross L E, et al, J. Mat. Sci, 1985, 20: 3745-3749. |
| [4] | Nagata K, Uchida Y, Okazaki K, et al, Japn. J. Appl. Phys, 1985, 24-2: 744-746. |
| [5] | Ting R Y, Halliyal A, Bhalla A S. Japn. J. Appl. Phys, 1985, 24-2: 982-983. |
| [6] | Browne J M, Lee C W, McColl J R, et al, IEEE, 1986. 300-303. |
| [7] | 张勤远,姜中宏,胡丽丽(ZHANG Qin-Yuan, et al).无机材料学报(Journal of Inorganic Materials), 1997, 12(3): 336-340. |
| [8] | Ding Y, Masuda N, Miura Y, et al, J. Non-crys. Solids, 1996, 203: 88-95. |
| [9] | Russel C R. J. Non-solids, 1997. 219, 212-218. |
| [10] | Donald W H. J. Non-cryst. Solids, 1979, 30: 301-315. |
| [11] | 唐有祺.结晶化学,北京,高等教育出版社,1957.120-140. |
| [12] | Markgray S A, Halliya A l, Bhalla A S, et al, Ferroelectric, 1985, 62: 17-26. |
| [13] | Ding Y, Osaka A, Miura Y. J. Non-crys. Solids, 1994, 176: 200-207. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%