采用溶胶-凝胶法制备并分析了掺杂铈、钕、铕、铒的MCM-41介孔材料,运用XRD、HRTEM、EDS和BET等方法考察了镧系金属元素掺杂对MCM-41结构的影响.研究结果表明,镧系金属元素掺杂到了MCM-41试样的骨架结构中.由于材料结构中的一部分Si4+被Ln3+所取代,介孔材料的有序孔道d值随着掺杂镧系离子半径的减小而降低,随着镧系元素掺杂量的增加而上升.
参考文献
| [1] | Yao H C, Yu Ya o. J. Catal, 1984, 86: 254-265. |
| [2] | 卢冠忠,汪仁.催化学报,1991,12:83-89. |
| [3] | Krege C T, Leonowicz M E, Roth W J, et al, Nature, 1992, 359: 710-712. |
| [4] | Beck J S, Vartuli J S, Roth W J, et al, J. Am. Chem. Soc, 1992, 114: 10843-10843. |
| [5] | Corma A, Fornes V, Carcia H, et al, J. Am. Chem. Soc, 1994, 116: 9767. |
| [6] | Leon R, Margolese D, Stukey G D, et al, Phys. Rev, 1995, 52: R2285. |
| [7] | Wu C G, Bein T. Science, 1994, 264: 1757-1759. |
| [8] | Beck J S, Kuehl G H, Olson D K, et al, US Patent, 1994, 5: 348-687. |
| [9] | Abe T, Tachibana Y, Takeshi Y, et al, Chem. Commun, 1995. 1617. |
| [10] | Tanev P T, Chibwe M, Pinnavania T J. Nature, 1994, 368: 321-324. |
| [11] | Wei D, Wang H, Feng X, et al, J. Phys. Chem. B, 1999, 103: 2113-2121. |
| [12] | Corma A. Chem. Rev, 1997, 97: 2373-2419. |
| [13] | He N-Y, Bao S-L, Xu Q-H. Stud. Surf. Sci. Catal, 1997, 105: 85. |
| [14] | Kuang Y, He N-Y. Colloid Surf. A: physicochem. Eng. Asp, 2001, 179: 177-184. |
| [15] | Araujo A S, Jaroniec M, Stud. J. Colloid Interface Sci, 1999, 218, 462-467. |
| [16] | Laha S C, Mukherjee P, Sainkar S R, et al, J. Catal, 2002, 207: 213-223. |
| [17] | Matos J R, Mercuri L P, Jaroniec M, et al, J. Mater. Chem, 2001, 11: 2580-2586. |
| [18] | Wang L Z, Shi J L, Yu J, et al, Nanostructure Materials, 1998, 10: 1289-1299. |
| [19] | Sing K S W, Evrett D H, Haul R A W, et al, Pure & Appl. Chem, 1985, 57 (4): 603-619. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%