研究了机械合金化制备PLZT陶瓷.实验结果表明, 采用纳米TiO2原料, 球磨5h就能得到PLZT粉体, 而采用微米TiO2原料, 球磨30h也只有少量的PLZT出现.可见纳米粉体在机械合金化制备PLZT粉体过程中起了重要的作用.机械合金化制备的PLZT粉体具有很好的烧结性能, 在1000℃的烧结条件下可以得到致密度达97%的PLZT陶瓷, 并且所得PLZT 陶瓷的压电性能和铁电性能与其它文献报道的相当.这为实现铁电陶瓷与电极低温共烧打下了基础.
参考文献
| [1] | Haertling G H, Land C L. it Ferroelectrics, 1972, 3: 269-280. |
| [2] | Haertling G H. it J. Am. Ceram. Soc., 1999, 82 (4): 797-818. |
| [3] | Kitaoka K, Kozuka H, Yoko T. it J. Am. Ceram. Soc., 1998, 81 (5): 1189-1196. |
| [4] | Cerqueira M, Nasar R S, it et al. Mater. Lett., 1998, 35: 166-171. |
| [5] | Das R N, Pathak A, it et al. J. Am. Ceram. Soc., 1998, 81 (12): 3357-3360. |
| [6] | Jiang J Z, Poulsen F W, it et al. J. Mater. Res., 1999, 14 (4): 1343-1352. |
| [7] | Simoneau M, L'Esperance G, it et al. J. Mater. Res., 1994, 9 (3): 535-540. |
| [8] | Jiang J Z, Lin R, it et al. J. Phys. D Appl., 1997, 30 (10): 1459-1467. |
| [9] | Kong L B, Ma J, Zhang T S. it J. Mater. Res., 2001, 16 (6): 1636-1643. |
| [10] | Poosanaas P, Uchino K. it Mater. Chem. Phys., 1999, 61: 36-41. |
| [11] | Damjanovic D, Demartin M. it Appl. Phys. Lett., 1996, 68 (21): 3046-3048. |
| [12] | Randall C A, Kim N, it et al. J. Am. Ceram. Soc., 1998, 81 (3): 677-688. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%