添加不同种类和含量的粘结剂,通过冷压和热压方法,结合炭化处理等不同工艺制备纳米碳管电极,利用DC-5电池测试仪分析其在盐水中的充放电性能,比较其电吸附比电容和等效电阻,发现当聚四氟乙烯(PTFE)的量为10%,聚偏氟二乙烯(PVDF)的量为15%时,电极可以冷压成型;酚醛树脂(PR)的量为20%时,电极可以热压成型,随着粘结剂的增加,电极在盐水中的电吸附比电容降低,等效电阻增大.通过纳米碳管电极表面结构、形貌、亲水性及在盐水中电吸附电容和等效电阻的分析,对其脱盐性能进行比较,发现添加20%PR粘结剂热压成型电极经炭化后,其比表面积大,内部孔隙丰富,亲水性好,在盐水中电吸附比电容大,等效电阻小,电吸附脱盐效果最为显著.
参考文献
| [1] | Semiat R,Galperin Y.Desalination,2001,140(1):27-46. |
| [2] | Demircioglu M,Kabay N,Kurucaovali I,et al.Desalination,,2003,153 (1-3):329-333. |
| [3] | Andelman M.Flow-through capacitor.US5192432,1993. |
| [4] | Otowa T.Planar,flow-through,electric,double-layer capacitor and a method of treating liguid with capacitor.US5538611,1996. |
| [5] | Oda H,Nakagawa Y.Carbon,2003,(41):1037-1047. |
| [6] | Odani A,Nimberger A,Markovsky B,et al.Journal of Power Sources,2003,119-121:517-521. |
| [7] | Cantalini C,Valentini L,Armentano I,et al.Journal of the European Ceramic Society,2004,24(6):1405-1408. |
| [8] | Chen J,Li W,Wang D,et al.Carbon,2002,(40):1193-1197. |
| [9] | 施利毅,谢建平,刘函宇,等.一种利用纳米碳管制造电极的电容式海水淡化处理方法.CN1463927A,2003. |
| [10] | Nakamura M,Nakanishi M,Yamamoto K.Journal of Power Sources.1996,60(2):225-231. |
| [11] | Gamby J,Taberna P L,Simon P,et al.Journal of Power Sources,2001,101(1):109-116. |
| [12] | Deyang Q,Hang S.J.Power Sources,1998,(74):99-107. |
| [13] | 王大志,陈冠民,徐才录,等(WANG Da-Zhi,et al).无机材料学报(Journal of Inorganic Materials),2001,16(4):672-676. |
| [14] | 张彬,马仁志,徐才录,等.电子学报,2000,28(8):13-15. |
| [15] | Li C,Wang D,Liang T,et al.Materials Letters,2004,58(29):3774-3777. |
| [16] | 申文忠,郑经堂.碳素技术,2002,4:5-9. |
| [17] | Nishino A.Tanso,1988,132:57-71. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%