Comparison of LSGM and LSGMC8.5 Synthesized by Advanced Pechini Method

用改进的柠檬酸法合成了具有钙钛矿结构的LSGM(La0.9Sr0.1Ga0.85Mg0.15O3-δ)和Co掺杂的LSGMC8.5(La0.9Sr0.1(Ga0.9Co0.1)0.85Mg0.15O3-δ).并从XRD、DTA-TG曲线、交流阻抗谱、电导率、密度和化学稳定性等方面比较了LSGM和LSGMC8.5的性能.从而探讨了Co掺杂对于LSGM性能的影响.结果表明相对于LSGM,Co的掺杂使立方钙钛矿结构的形成温度由1400℃降低到1300℃左右,离子电导率由3.85×10-2上升到5.38×10-2S/cm,密度由理论密度的95%上升到99%.因此Co的掺杂使LSGM的各方面性能都有了一定的提高,LSGMC8.5比LSGM更适合做中温SOFC的电解质材料.

参考文献

[1]	Ishihara T,Matsuda H,Takita Y.J.Am.Chem.Soc.,1994,116:3801-3803.
[2]	Huang P,Petric A.J.Electrochem.Soc.,1996,143:1644-1648.
[3]	Huang K,Feng M,Goodenough J B.J.Am.Ceram.Soc.,1996,79:1100-1104.
[4]	Maric R,Ohara S,Fukui T,et al.J.Electrochem.Soc.,1999,146:2006-2010.
[5]	Ishihara T,Furutani H,Honda,et al.J.Chem.Mater.,1999,11:2081-2088.
[6]	Yamada T,Chitose N,Akikusa J,et al.Development of intermediate-temperature SOFC module using doped lanthanum gallate.In Proceedings of the EighthInternational Symposium on Solid Oxide Fuel Cells (SOFCⅧ),ed.C.Singhal and M.Dokiya.The Electrochemical Society Inc.,Pennington,NJ,USA,2003.113-118.
[7]	Huang K,Goodenough J B.J.Sol.State Chem.,1998,136:274-283.
[8]	Tas A C,Majewski P,Aldinger F.J.Am.Ceram.Soc.,2000,83:2954-2960.
[9]	Majewski P,Rozumek M,Tas C A,et al.J.Electroceram.,2002,8:65-73.
[10]	Stevenson J W,Armstrong T R,McCready D E,et al.J.Electrochem Soc.,1997,144 (10):3613-3620.
[11]	Bauerle J E.J.Phys Chem Solids.,1969,30:265-267.
[12]	郑文君,武丽艳,彭定坤,等(ZHAENG Wen-Jun,et al).无机材料学报(Journal of Inorganic Materials),2001,16(2):358-362.
[13]	Zha S,Xia C,Fang X,et al.Ceram.Int.,2001,27:649-654.
[14]	Saiful Islam M,Andrew Davies R.J.Mater.Chem.,2004,14:86-93.
[15]	Trofimenko N,Ullmann H.J.Solid State Ionics,1999,118:215-227.
[16]	Kim J H,Yoo H I.J.Solid State Ionics,2001,140:105-113.
[17]	Ishihara T,Shibayama T,Ishikawa S,et al.J.Journal of the European Ceramic Society,2004,24:1329-1335.
[18]	Watanabe M,Uchida H,Yoshida M.J.Electrochem.Soc.,1997,144:1739-1743.
[19]	Yamaji K,Horita T,Ishikawa M,et al.J Electrochemical Soc.,1997,40:1041-1050.

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网