微波烧结(Microwave Sintering)是一种新型、高效的烧结技术,具有传统烧结技术无可比拟的优越性.本文在不添加任何烧结助剂的前提下,采用高纯微米级氮化铝(AlN)粉,在1700℃/2h的微波低温烧结工艺条件下制备出透明度较高的AlN透明陶瓷.分析结果表明,采用微波低温烧结工艺制备的AlN透明陶瓷晶粒尺寸细小(＜10μm),晶粒发育完善且分布均匀,晶界平直光滑且无第二相分布,从而证明用微波烧结可以实现AlN透明陶瓷的低温烧结.
参考文献
| [1] | Coble R L.Transparent alumina and method of preparation.U.S.Pat.No.3026210,Mar.10,1962. |
| [2] | Kuramoto N,Taniguchi H.Journal of materials sciengce letters,1984,3:471-474. |
| [3] | Zhou Y P,et al.Journal of Inorganic materials,1999,14 (4):674-678. |
| [4] | 刘军芳,付正义,张金咏,等.陶瓷学报,2001,22(3):157-160. |
| [5] | Cheng J P,Agrawal D,Zhang Y J,et al.Focus on Electronics,2000,9:71-74. |
| [6] | Watari K,Valecillos M C,Brito M E,et al.J.Am.Ceramic.Soc.,1996,79 (12):3103-3108. |
| [7] | Miao W G,Wu Y,Zhou H P,et al.J.Mater.Sci.Lett.,1997,16:1245-1246. |
| [8] | Kuramoto N,Taniguchi H,Aso I.J.Ceram.Bullet,1989,68:883-887.[9]Bachelard R,Joubert.Mater.Sci.Eng.,1989,9:247-251. |
| [9] | Kuramoto N,Taniguchi H,Aso I.J.Ceram.Bullet,1989,68:883-887.[9]Bachelard R,Joubert.Mater.Sci.Eng.,1989,9:247-251. |
| [10] | 胡晓力,陈楷,严虹.中国陶瓷.1995,31(1):29-32 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%