采用喷射-共沉淀法制备了纳米晶Ni1-xZnxFe2O4(0≤x≤1.0)铁氧体粉料.通过TG-DSC、XRD、SEM、TEM、BET等测试手段分析了其微观结构和形貌,用振动样品磁强计测量其室温下磁性能.结果表明:喷射-共沉淀法制备的粉料颗粒细小均匀、形状完整.600℃下煅烧1.5h,样品晶粒尺寸为30nm左右,平均颗粒尺寸＜100nm.室温下,样品比饱和磁化强度随Zn2+含量增加而变化,当x=0.5时,最大比饱和磁化强度σs为66.8A·m2/kg.当晶粒大小为41nm时,纳米晶Ni0.5Zn0.5Fe2O4铁氧体矫顽力达到最大值5.06kA/m,随后又随晶粒尺寸增大而减小.这归因于纳米晶软磁材料中强烈的无序磁晶各向异性模式的影响.
参考文献
| [1] | Dorman J L,Fiorani D.J Magn.Magn.Mater.,1995,140-144:415-418. |
| [2] | Kodama R H.J Magn.Magn.Mater.,1999,200:359-372. |
| [3] | Zhengxing Yue,Ji Zhou,Longtu Li,et al.J Magn.Magn.Mater.,2000,208:55-60. |
| [4] | Buschow K H.J.Handbook of Magnetic Materials,First Edition.Amsterdan:North-Holland Co.,2003. |
| [5] | Suryanarayana C.International Mater.Rev.,1995,2:41-63. |
| [6] | 张立德,牟季美.纳米材料和纳米结构.北京:科学出版社,2001. |
| [7] | 文雯,张怀武,钟慧.磁性材料及器件,2005,36(3):24-26. |
| [8] | 任晓燕,徐振佩,何正明.材料研究学报,2004,18(3):315-320 |
| [9] | Islam M U,Abbas T,Shahida B Niazi,et al.Solid State Communications,2004,130:353-357. |
| [10] | 孙杰,刘建华,李松梅(SUN Jie,et al).无机材料学报 (Journa1 of Inorganic Materials),2005,20 (5):1077-1082. |
| [11] | 李萌远,李国栋.铁氧体物理学.北京:科学出版社,1978. |
| [12] | 都有为.材料导报,2001,15(7):6-8. |
| [13] | Herzer G.Scripta Metall.Mater.,1995,33 (10/11):1741-1750. |
| [14] | David J.Sellmyer,Yi Liu,D.Shindo,Handbook of Advanced Magnetic Materials,First Edition.Beijing:Tsinghua University Press,2005. |
| [15] | 王丽,周庆国,孙建荣,等.磁性材料及器件,2006,37(1):23-25. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%