采用水热法制备了不同晶型CdSe纳米棒,并用TEM、SEM、XRD、TGA-DTA对其进行了表征.结果显示反应温度为240℃生成纤锌矿型CdSe纳米棒,反应温度为200℃生成闪锌矿型CdSe纳米棒.并对纳米棒进行了光电性能测定,纤锌矿型CdSe纳米棒膜电极的光电转换效率(IP.CE)优于闪锌矿型CdSe纳米棒膜电极的IPCE.CdSe/PMeT复合膜电极在具有最大光电转换效率时的波长发生了红移.
参考文献
| [1] | 聂秋林,袁求理,徐铸德(NIE Qiu-Lin,et al).无机材料学报(Journal of Inorganic Materials),2004,19(6):1411-1414. |
| [2] | 赵启涛,候利松,黄瑞安,等(ZHAO Qi-Tao,et al).无机材料学报(Journal of Inorganic Materials),2004,19(3):477-480. |
| [3] | 曹广胜,俞庆森,董喜贵,等(CAO Guang-Sheng,et al).无机材料学报(Journal of Inorganic Materials),2005,20(4):815-820. |
| [4] | 张俊松,马娟,陈秀梅,等.南京师大学报,2004,27(2):61-62. |
| [5] | Li Y D,Liao H W,Ding Y,et al.J.Chem.Mater.,1998,10 (9):2301-2303. |
| [6] | Wang W Z,Geng Y,Yan P,et al.Inorgnic Chemistry Communications 2,1999.83-85. |
| [7] | Yu S H,Wu Y S,Yang J,et al.J.Chem.Mater.,1998,10:2309-2312. |
| [8] | Xu D S,Shi X S.J.Phys.Chem.,2000,104 (21):5061-5063. |
| [9] | Trindade T,O' Brien P,et al.J.Mater.Chem.,1996,6(3):343-346; Adv.Mater.,1996,8 (2):161-163. |
| [10] | Trindade T,O' Brien P,et al.J.Mater.Chem.,1996,6(3):343-346; Adv.Mater.,1996,8 (2):161-163. |
| [11] | Huynh W U,Peng X G,Alivisatos A P.Adv.Mater.,1999,(11):923-927. |
| [12] | Huynh W U,Pittmer J J,Trclemariam D J,et al.Phys.Rev.,2003,67 (11):115326-115331. |
| [13] | Manna L,Milliron D J,Meisel A.Nat.Mater.,2003,2:382-386. |
| [14] | Peng Q,Dong Y J,Deng Z X,et al.Inorg.Chem.,2002,41 (20):5249-5254. |
| [15] | 李东升,吕功煊.高等学校化学学报,2002,23(4):685-689. |
| [16] | Liu J S,Tanaka T,Sivula K,et al.J.Am.Chem.Soc.,2004,126:6550-6551. |
| [17] | 郝彦忠,蔡春立.物理化学学报,2005,21(12):1395-1398. |
| [18] | Snaith H J,Whiting G L,Sun B,et al.Nano Letters,2005,5 (9):1653-1657. |
| [19] | 郝彦忠,武文俊.化学学报,2005,63(3):215-218. |
| [20] | 武文俊,郝彦忠.感光科学与光化学,2004,22(5):378-382. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%