利用固相反应烧结法制备了层状钙钛矿锰氧化物LaSr2Mn2-xCuxO7多晶样品.通过X射线衍射仪、超导量子干涉仪、直流四探针法对其结构和磁性、电特性进行了研究.结果表明,样品均为Sr3Ti2O7型单相多晶,属四方晶系,空间群为I4/mmm.10%Cu的替代,破坏了LaSr2Mn2O7的电荷有序态,从而呈现出一种典型的自旋玻璃特性,在T=225K发生自旋冻结.电性测量表明,Cu的替代,破坏了LaSr2Mn2O7的导电特性,使此材料在整个观察的温区呈现绝缘体特性,进一步影响了其输运性性.
参考文献
| [1] | Myron B Salamon,Marcelo Jaime.Rev.Mod.Phys.,2001,73 (3):583-628. |
| [2] | 祝向荣,沈鸿烈,沈勤我,等(Zhu Xiangrong,et al).无机材料学报(Journal of Inorganic Materials),1999,14(6):915-920 |
| [3] | Sunil Nair,Banerjee A.Phy.Rev.B,2004,70 (11):104427-104431. |
| [4] | Joongoe Dho,Kim W S,Hur N H.Phy.Rev.B,2001,65(9):24404-24409. |
| [5] | Motitomo Y,Asamitsu A,Kuwahara H,et al.Nature,1996,380 (2):141-144. |
| [6] | Wilkins S B,Spencer P D,Beale T A.Phy.Rev.B,2003,67 (8):205110-205114. |
| [7] | Subhayan Biswas,Sandip Chatterjee,Chatterjee P,et al.Phy.Rev.B,2002,66 (7):214403-2114409. |
| [8] | Weigand F,Gold S,Schmid J,et al.Appl.Phy.Lett.,2002,81 (9):2035-2037. |
| [9] | 鲁毅,李庆安,邸乃力,等.物理学报,2003,52(6):1520-1523. |
| [10] | Sun J R,RaoG H,GaoXR,et al.J.Appl.Phy.,1999,85(7):3619-3622. |
| [11] | Kallel N,Dezanneaub G,Dhahria J,et al.J.Magn.Magn.Mater.,2003,261 (1):56-65. |
| [12] | Yuan X B,Liu Y H,Yin N,et al.J.Magn.Magn.Mater.,2006,306 (2):167-171. |
| [13] | Mydosh J A.Spin glass.London:Taylor and Francis.1993.1-100. |
| [14] | 陈春霞,章建辉,钱天,等.材料科学与工程学报,2005,23(1):23-27. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%