采用直流电解合成法,分别以CeCl3,Ce(NO3)3,CeCl3-KI溶液为电解液单室制备了纳米CeO2粉体.经高温焙烧后,TEM和XRD测试表明:粒子基本呈球形,所得产物均为立方晶系CeO2,粒径分别为20～50 nm,30～50 nm,20～100 nm.同时,使用阴离子交换膜的双室电解法电解CeCl3溶液,发现得到的CeO2粒径(7～20nm)比单室电解得到的小,分析了造成粒径不同的原因.本工作还对各溶液体系电解形成CeO2的机理进行了分析.
参考文献
| [1] | Therese G H A,Kamath P V.Chem.Mater.,2000,12(5):1195-1204. |
| [2] | Paunovic M,Schlesinger M.Fundamentals of Electrochemical Deposition.John Wiley & Sons,Inc:New York,1998.1. |
| [3] | Cogle R T,Switzer J A.Electrochemical synthesis of ceramic films and powders.U.S.Pat.,4882014.1989-11. |
| [4] | Zhou Y,Switzer J A.J.Alloy Compd.,1996,237 (1-2):1-5. |
| [5] | Chaim R,Almaleh R S,Gal-Or L.J.Am.Ceram.Soc.,1994,77 (12):3202-3208. |
| [6] | Peulon S,Lincot D.Adv.Mater.,1996,8 (2):166-170. |
| [7] | Zhitomirsky I.Nanostructured Materials,1997,8 (4):521-528. |
| [8] | Therese G H A,Kamath P V.Chem.Mater.,1999,11(12):3561-3564. |
| [9] | Zhitomirsky I,Gal-Or L.J.Mater.Sci.,1998,33 (3):699-705. |
| [10] | Gal-Or L,Sibermar I,Chaim R.J.Electrochem Soc.,1991,138 (12):1939-1942. |
| [11] | 景介辉,孙都城,马利亚马木提(JING Jie-Hui,et al).中国稀土学报(Chin.Rare Earth),2005,23(增刊):58-61 |
| [12] | 王中林主编,曹茂盛,李金刚译.纳米材料表征.北京:化学工业出版社,2005. |
| [13] | Tsunekawa S,Sivamohan R,Ito S,et al.Nanostructured Materials,1999,11 (1):141-147. |
| [14] | Li F-B,Newman R C,Thompson G E.Electrochim.Acta.,1997,42 (16):2455-2464. |
| [15] | 吕德义,卞飞荣,许可(LüDe-Yi,et al).无机材料学报(Journal of Inorganic Materials),2007,22(1):59-64. |
| [16] | 景介辉,孙都城,徐秀梅(JING Jie-Hui,et al).无机材料学报(Journal of Inorganic Materials),2006,21(1):53 57. |
| [17] | 梅燕,韩业斌,聂祚仁(MEI Yan,et al).中国稀土学报(Chin.Rare Earth),2006,24(1):43-47. |
| [18] | 李永军,刘春艳.有序纳米结构薄膜材料,第一版.北京:化学工业出版社,2006. |
| [19] | 李小忠,王连军,赵铭(LI Xiao-Zhong,et al).无机化学学报(Chinese J.Inorg.Chem),2006,22(1):79-82. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%