以硅藻土为原料,混合部分硅溶胶与少量晶种导向剂进行成型,然后进行汽相转化,制备了无粘结剂小晶粒ZSM-5沸石.晶种导向剂中的沸石微晶和结构单元诱导硅铝原料转化为交错生长的ZSM-5沸石,导致无粘结剂沸石的生成.产物的表征结果表明,制备的无粘结剂小晶粒ZSM-5成型沸石具有丰富的孔结构,较大的比表面以及较高的机械强度,酸性质可调,可用作催化材料或吸附剂.
参考文献
| [1] | Breck D W.Zeolite Molecular Sieves,Wiley,New York 1974. |
| [2] | Camblorm M A,Corma A,Martinez A,et al.Appl.Catal.A,1989,55 (1):65-74. |
| [3] | Shiralkar V P,Joshi P N,Eapen M J,et al.Zeolites,1991,11 (5):511-516. |
| [4] | van der Pol A J H P,Verduyn A J,van der Hooff J H C,et al.Appl.Catal.A,1992,92 (2):113-130. |
| [5] | Arribas M A,Martinez A.Catal.Today,2001,65 (2):117-122. |
| [6] | Holland B T,Abrams L,Stein A.J.Am.Chem.Soc.,1999,121 (17):4308-4309. |
| [7] | Lee Y,Lee J S,Park Y S,et al.Adv.Mater,2001,13 (16):1259-1263. |
| [8] | Valtchev V.J.Mater.Chem.,2002,12 (6):1914-1918. |
| [9] | Rauscher M,Selvam T,Schwieger W,et al.Mieroporous Mesoporous Mater.,2004,75 (3):195-202. |
| [10] | Long YC 1998 CN1037415. |
| [11] | Nakahira A,Takezoe S,Yamasaki Y.Chem.Lett.,2004,33 (10):1400-1401. |
| [12] | Dong A G,Wang Y J,Tang Y,et al.Adv.Mater.,2002,14 (20):1506-1510. |
| [13] | Dong A G,Wang Y J,Tang Y,et al.Adv.Mater.,2002,14 (12):926-929. |
| [14] | Mintova S,Holzl M,Valtchev V,et al.Chem.Mater.,2004,16 (25):5452-5459. |
| [15] | 王德举,朱桂波,张亚红,等 (WANG De-Ju,et al).无机材料学报 (Journal of Inorganic Materials),2005,20 (3):635-640. |
| [16] | Xu W Y,Dong J X,Li J P,et al.J.Chem.Soc.Chem.Commun.,1990.755-756. |
| [17] | Anderson M W,Holmes S M,Hanif N,et al.Angew.Chem.Int.Ed.,2000,39:2707-2710. |
| [18] | Wang Y J,Tang Y,Dong A G,et al.J.Mater.Chem.,2002,12 (6):1812-1818. |
| [19] | Wang D J,Tang Y,Dong A G,et al.Chinese Chem.Lett.,2003,14 (12):1299-1302. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%