采用共沉淀法制备了掺钒钛酸铋粉体,研究了粉体的晶化过程、微观形貌和烧结性能.与传统固相反应法相比,共沉淀法合成钛酸铋相的反应可在550℃完成,比固相反应法低250℃左右,所得粉体的粒径＜100nm.此外,共沉淀法制备的粉体具有良好的烧结性能,在900℃达到理论密度的96%.与固相法烧结陶瓷相比,共沉淀粉体制备的材料具有更低的介电损耗.
参考文献
| [1] | Park P H,Kang B S,Bu S D,et al.Nature (London),1999,401 (6754):682-684. |
| [2] | Takenaka T,Sakata K.J.Appl.Phys.,1984,55 (4):1092-1099. |
| [3] | Toda K,Takenaka T,Sakata K.J.Appl.Phys.,1984,56(7):2187-2188. |
| [4] | Joshi P C,S.Krupanidhi B.J.Appl.Phys.,1992,72(12):5827-5833. |
| [5] | Horn J A,Zhang S C,Selvaraj U,et al.J.Am.Ceram.Soc.,1999,82 (4):921-926. |
| [6] | Prasada Rao A V,Robin A I,Komarnani S.Mater.Lett.,1996,28 (4-6):469-473. |
| [7] | Pookmanee P,Uriwilast P,PhanichpantChen S.Ceram.Int.,2004,30 (7):1913-1915. |
| [8] | 阚艳梅,靳喜海,王佩玲,等(KAN Yan-Mei,et al).无机材料学报(Journal of Inorganic Materials),2002,17(1):51-55. |
| [9] | Tomar M S,Melgarejo R E,Hidalgo A,et al.Appl.Phys.Lett.,2003,83 (2):341-343. |
| [10] | Chon U,Shim J S,Jang H M.Solid State Commun.,2004,129 (7):465-468. |
| [11] | Yao Y Y,Song C H,Bao P,et al.Appl.Phys.Lett.,2004,95 (6):3126-3130. |
| [12] | Chaudhuri A R,Laha A,Krupanidhi S B.Solid State Commun.,2005,133 (9):611-614. |
| [13] | Werner P E.Ark.Kemi.,1964,31:513-516. |
| [14] | Tang Q Y,Kan Y M,Li Y G,et al.Script Mater.,2006,54 (12):2075-2080. |
| [15] | Shen Z J,Liu J,Grins J,et al.Adv.Mater.,2005,17(6):676-680. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%