利用动态Hopkinson装置和Instron 4026测试了15%SiCP/Al-5Cu、 15%SiCP/2124、15%SiCP/Al-Li、15%SiCW/6061和30%SiCP/6061铝合金等几种复合材料的准静态和冲击力学性能，探讨了应变率等对于强度、硬化模量和失效应变等的影响。同时观察了上述材料动态拉伸断口，揭示了金属基复合材料破坏的几种不同控制机理。最后讨论了实验中发现的上述复合材料拉压不对称性的新特征，其中考虑了金属基复合材料的热失配应力和不同的损伤、破坏控制机理。
In this paper, the mechanical behaviors of 2124, Al-5Cu, Al-Li and 6061 alloys reinforced by silicon carbide particulate, together with the silicon carbide whisker reinforced 6061 Al alloy, were studied under quasi-static and impact loading conditions, by using the Split Hopkinson Tension / Compressure Bars and Instron universal testing machine. The effect of the strain rate on the UTS, hardening modulus, and failure strain was investigated. At the same time, the SEM observations of dynamic fracture surfaces of various MMC materials showed some distinguished failure characteristics, which determined the sensitivity of the strain rate of failure strain and the asymmetry of tension and pressure of MMC materials. Some new characteristics of asymmetry of mechanical behaviors of MMC materials under tension and compression loadings were also presented and explained in details in this paper, which can be considered as flags, to some degree, to determine the controlling mechanism of damage and failure of metal matrix composites under impact loading. The development of new constitutive laws about MMC materials under impact loadings should benefit from these experiment results and theoretical analysis
参考文献
| [1] | ［1］ Clyne T W, Withers P J. An introduction to metal matrix composites ［M］. Cambridge: Cambridge University Press, 1993. |
| [2] | ［2］ Bless S J, Jurick D J, Imothy S P. Penetration and dynamic properties of metal matrix composites［A］. In: Meyers M A ,ed. Int conf high strain rate phenomena in materials［C］. Sandiego: Plenum Press, 1990.1051-1058. |
| [3] | ［3］ Marchand A, Duffy J, Christman T A, Suresh S. Experimental study of the dynamic mechanical properties on Anal-SiCW［J］． Engng Fract Mech， 1988,30： 295-303. |
| [4] | ［4］ Pickard S M, Derby B, Harding J, Taya M. Strain rate dependence of failure in 2124 Al/SiC whisker composite［J］. Failure in Composite, 1988,22： 601-606. |
| [5] | ［5］ Vaidya R U, Song S G, Zurek A K. Dynamic mechanical response and thermal expansion of ceramic particle reinforced aluminum 6061 matrix composites［J］. Phil Magzine A, 1994,70： 819-836. |
| [6] | ［6］ Tvergaard V． Analysis of tensile properties for a whisker-reinforced metal-matrix composite［J］. Acta Mater， 1990,38： 185-195. |
| [7] | ［7］ Lloica J, Needleman A, Suresh S. An analysis of the effects of matrix void growth on deformation and ductility in metal-ceramic composites［J］. Acta Metall Mater， 1991,39：2317-2335. |
| [8] | ［8］ Vaidya R U, Zurek A K． Dynamic mechanical response of an SiCP/Al-Li(8090) composite［J］. J of Mater Sci， 1995,30： 2541-2548. |
| [9] | ［9］ Hong S I, Gray III G T, Lewandowski J J. Dynamic deformation behavior of Al-Zn-Mg-Cu alloy matrix composites reinforced with 20 vol% SiC［J］. Acta Mater， 1993,41： 2337-2351. |
| [10] | ［10］ 黄晨光. 几种金属材料的动态力学性能和激光辐照下结构的热力耦合破坏［D］．北京：中国科学院力学研究所，1996. |
| [11] | ［11］ Klepaczko J R. Microscopic deformation mechanism of metal under impact loading［A］. In: Harding, et al, eds. Int conf mech prop mater at high rate of strain［C］. Oxford Bristol: Institute of Physics, 1989. 283-298. |
| [12] | ［12］ Cobbin S F, Wilkinson D S. Influence of matrix strength and damage accumulation on the mechanical response of a particulate metal matrix composite［J］. Acta Metall Mater, 1994,42:1311-1318. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%