对单向M40J/5228A复合材料进行了真空热循环试验(93～413 K,10-5Pa).分别测试了经不同次数真空热循环后材料的质损率及线膨胀系数.通过所建二维细观损伤模型分析了真空热循环次数对材料线膨胀系数曲线影响的原因.试验结果表明,随真空热循环次数的增加,质损率增大,并经约48次真空热循环后趋于平缓;横向线膨胀系数随温度升高而线性增大,真空热循环次数对其没有影响;纵向线膨胀系数在原始状态时随温度升高而线性减小,经113次真空热循环后表现出先下降后上升的非线性特征,真空热循环次数对纵向线膨胀系数的影响,与界面脱粘程度和残余应力的消除密切相关.
参考文献
| [1] | 张建可.树脂基碳纤维复合材料的热物理性能之一--热膨胀[J].中国空间科学技术,1987 (5):45-50. |
| [2] | 肖少伯,刘志雄.卫星结构轻型化与复合材料应用[J].宇航材料工艺,1993 (4):1. |
| [3] | Dauphin J. Materials in space: Working in a vacuum[J]. Vacuum, 1982, 32 (10/11): 669. |
| [4] | ESA/PSS-09/QRM-02T Issue 2. A screening method employing a thermal vacuum for the selection of materials to be used in space [S]. 1976. |
| [5] | ESA/PSS-43/QRM-31T Issue 1. A screening test method employing a thermal vacuum for the selection of materials to be used in the manufacture of spacecraft optical devices [S]. 1978. |
| [6] | Campbell W A, Marriott R S, Park J J. Outgassing data for selecting spacecraft materials[R]. NASA N88-10117 MF. NASA, 1987. |
| [7] | 王玉林,万怡灶,陈桂才,等.三维编织碳纤维/环氧复合材料的吸湿特性及外应力的影响[J].复合材料学报,2002,19 (6):101-105. |
| [8] | 曾竟成,罗青.复合材料理化性能[M].长沙:国防科技大学出版社,1998.51-53. |
| [9] | 陈平,刘胜平.环氧树脂[M].北京:化学工业出版社,2002.167-168. |
| [10] | 过梅丽.高聚物与复合材料的动态力学热分析[M]. 北京:化学工业出版社,2002.42-43. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%