研究了针刺毡预制炭/炭复合材料(C/C)经不同温度石墨化处理后的磁电阻特性.结果表明:实验材料磁电阻于各位向(0°～180°)均相等,且石墨化处理温度越高,材料的磁电阻越大,外磁场强度、测量温度等因素不影响磁电阻-位向关系;在同一磁场强度下,石墨化处理温度高的材料磁电阻为正值,石墨化处理温度低时磁电阻为负值,且磁电阻与测量温度(5～300 K)呈线性关系变化,高于一定测量温度后,磁电阻稳恒为0;磁电阻-测量温度曲线回归方程的斜率随热处理温度的增加而降低,且斜率-热处理温度的变化曲线与材料的晶面间距d(002)随热处理温度的变化曲线形状类似;测量温度相同时,磁电阻随外加磁场强度的增大而增大,在低场强(低于1.2×107A/m)下,呈现二次函数关系,当场强高于1.2×107A/m,磁电阻-磁场强度关系为线性;不同场强下,随石墨化处理温度的提高,磁电阻也增大.
参考文献
| [1] | 稻恒道夫,白石稔,中溝実,等.黑铅程度の评价[J].炭素(日),1984(118):165-175. |
| [2] | 菱山幸宥.炭素の磁抵抗效果[J].炭素(日),1981(107):149-161. |
| [3] | Buckly John D. Carbon-Carbon Materials and Composites[M]. New Jersey, U S A: Noyes Publications Park Ridge,1993. 105-149. |
| [4] | Savage G. Carbon-Carbon Composites [M]. London: Chap man & Hall, 1993. 323-343. |
| [5] | Fitzer E. The future of carbon-carbon composites [J] .Carbon, 1987, 25(2): 163-190. |
| [6] | Tanaka H, Kaburagi Y, Kimura S. Graphitization behaviour of carbon fibre glassy carbon composites [J]. J Materials Science, 1978, 13: 2555-2559. |
| [7] | 孙立,邓海金,李明,等.不同测试位向C/C复合材料磁电阻效应[J].复合材料学报,2003,20(3):47-51.Sun Li, Deng Haijin, Li Ming, et al. Magnetoresistance of C/C composite in different measuring orientations [J]. Acta Materiae Compositae Sinica , 2003, 20(3): 47-51. |
| [8] | 邓海金,李明,孙立,等.石墨化处理对炭/炭复合材料磁电阻特性的影响研究[J].新型炭材料,2003,18(2):89-94.Deng Haijin, Li Ming, Sun Li, et al. Influence of graphitization treatment on the characteristic of magnetoresistance of carbon-carbon composite [ J]. New Carbon Materials,2003, 18(2): 89-94. |
| [9] | 邓海金,李明,孙立,等.短切纤维炭/炭复合材料样品的磁电阻特性研究[J].新型炭材料,2004,19(3):219-223.Deng Haijin, Li Ming, Sun Li, et al. The magnetoresistance characteristic of C/C composites with short carbon fiber at different heat treatment temperatures [J]. New Carbon Materials, 2004, 19(3): 219-223. |
| [10] | Inagaki M, Harada S, Saato T. Carbonization of polyimide film: Kapton [J]. Carbon, 1989, 27(2): 253-257. |
| [11] | Dobbs R. Electricity and Magnetism [M]. London, Boston: Routledge & K Paul, 1984. |
| [12] | Yoshida A, Kaburagi Y, Hishiyama Y. Microtexture and magnetoresistance of glass-like carbons [J]. Carbon, 1991,29(8): 1107-1111. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%