采用改性单体原位反应聚合法(MPMR)制备了苯炔基封端的聚酰亚胺树脂,采用模压方法研究了聚酰亚胺复合材料的成型工艺.所制备的树脂和复合材料均具有很高的热稳定性;复合材料在371℃的力学性能保持率高于室温力学性能的50%;其玻璃化转变温度为449℃;纯树脂和复合材料在371℃空气中100 h的热失重小于3%.所研制的聚酰亚胺复合材料基本满足了371℃高温树脂的性能.
参考文献
| [1] | Scola D A,Wai M.The thermo-oxidative stability of fluorinated polyimides and polyimides/graphite composites at 371℃[J].J Appl Polym Sci,1994,52:421-429. |
| [2] | Scola D A,Vontell J H.Process characteristics of high tem-perature polymers and composites[A].In:34th Int SAMPE Symp[C].USA:Society for the Advancement of Material and Process Engineering,1989:88-97. |
| [3] | Pater R H.Thermosetting polyimides:a review[J].SAMPE J,1994,30(5):29-38. |
| [4] | Brown A S.The high air force finds an ultrahigh temperature resin[J].AeroAm,1991:56-57. |
| [5] | Serafini T T,Devlvigs P,Lightsey G R.Thermally stable polyimides from solutions of monomeric reactants[J].J Appl Polym Sci,1972,16:905-915. |
| [6] | Wilson D.PMR-15 processing,properties and problems[J].Brit Polym J,1988,20:405-416. |
| [7] | Kantz M.Processing of PMR-15 prepregs for high temperature composites[J].Plastics Engineering,1990,46(1):27-30. |
| [8] | Russell J D,Kardos J L.Kinetics of imidization and crosslinking for AFR-700B polyimide[A].In:41st Int SAMPE Symp[C].USA:Society for the Material and Process Engineering,1996:120-134. |
| [9] | Vannucci R D,Cifani D.700 F(371 ℃) properties of autoclave cured PMR-Ⅱ composites[J].Soc Adv Mat Proc Eng,1988:562-575. |
| [10] | Florence M,Loustalot G.New thermostable synthesis:structure property relationships of nadic terminated telechelic fluorine polyimides[J].Polym Int,1996,41:135-149. |
| [11] | 王震.聚酰亚胺的复合材料制备与辐射固化[D].长春:中国科学院长春应用化学研究所,2002. |
| [12] | 王震,益小苏,丁孟贤.含联苯结构的聚酰亚胺复合材料的研究[J].复合材料学报,2003,20(3):27-30.Wang Zhen,Yi Xiaosu,Ding Mengxian.Study on polyimide composite containing biphenyl structure[J].Acta Materiae Compositae Sinica,2003,20(3):27-30. |
| [13] | Chu Q,Zhang J,Xu Z,Ding M,etal.Study on a novel polyimide precursor prepared by a modified polymerization of monomeric reactants (MPMR) procedure[J].Macromol Chem Phys,2000,201:505-509. |
| [14] | Meyer G W,Glass T E,Grubbs H J,et al.Synthesis and characterization of polyimides endcapped with phenylethynyl anhydride[J].J Polym Sci,Part A:Polym Chem,1995,33:2141-2149. |
| [15] | Takekokoi T,Terry J M.High-temperature thermoset polyimides containing disubstituted acetylene end groups[J].Polymer,1994,35(22):4874-4880. |
| [16] | Hergenrother P M.Composites for high speed civil transports[J].SAMPEJ,1999,35(1):30-32. |
| [17] | Hergenrother P M,Connell J W,Smith J G.Phenylethynyl containing imide oligomers[J].Polymer,2000,41:5073-5081. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%