以全氢聚硅氮烷(PHPS)和聚甲基硅氮烷(PHMS)为陶瓷先驱体,通过循环浸渍和600℃低温裂解分别制备了三维石英纤维增强氮化硅复合材料,对比研究了复合材料的力学性能和微观结构.结果表明:由PHPS制备的复合材料密度为1.83 g/cm3,气孔率10%,弯曲强度45.4 MPa,材料断口平整,纤维基体界面结合强;而由PHMS制备的复合材料密度仅为1.66 g/cm3,气孔率16%,却具有更高的弯曲强度56.3 MPa,材料断面较粗糙,界面结合较弱.先驱体活性不同是导致复合材料界面结合强弱及力学性能不同的主要原因.
参考文献
[1] | Brazel J P,Fenton R.ADL-4D6:A silica/silica composite for hardened antenna windows[C]//Proceedings of the 13th symposium on electromagnetic windows.Atlanta:Publishing House of Georgia Institute of Technology,1976:9-16. |
[2] | Manocha L M,Panchal C N,Manocha S.Silica/silica composites through electrophoretic infiltration--Effect of processing conditions on densification of composites[J].Sci Eng Comp Mater,2000,9(4):219-230. |
[3] | 田焕芳.石英增强磷酸盐复合材料制备和组织结构及力学性能[D].哈尔滨:哈尔滨工业大学,2003:1-73. |
[4] | 郑文伟,陈朝辉,方晖,等.热模压辅助先驱体浸渍裂解制备Cf/SiC复合材料研究[J].复合材料学报,2003,20(5):44-48.Zheng Wenwei,Chen Zhaohui,Fang Hui,et al.Fabrication of Cf/SiC composites via precursor infiltration and pyrolysis assisted by hot-pressing[J].Acta Materiae Compositae Sinica,2003,20(5):44-48. |
[5] | 简科,陈朝辉,马青松,等.裂解工艺对先驱体转化制备Cf/SiC材料结构与性能的影响[J].复合材料学报,2004,21(5):57-61.Jian Ke,Chen Zhaohui,Ma Qingsong,et al.Effect of pyrolysis process on the microstructure and mechanical properties of Cf/SiC composites fabricated by precursor pyrolysis[J].Acta Materiae Compositae Sinica,2004,21(5):57-61. |
[6] | Qi G J,Zhang C R,Hu H F,et al.Preparation of three-dimensional silica fiber reinforced silicon nitride composites using perhydropolysilazane as precursor[J].Mater Lett,2005,59(26):3256-3258. |
[7] | Isoda T,Kaya H,Nishii H,et al.Perhydropolysilazane precursors to silicon nitride ceramics[J].J Inorgan Organomet Polym,1992,2(1):151-160. |
[8] | Seyferth D,Wiseman G H.High-yield synthesis of Si3N4/SiC ceramic materials by pyrolysis of a novel polyorganosilazane[J].J Am Ceram Soc,1984,67(7):132-133. |
[9] | Seyferth D,Wiseman G H.Preceramic organosilazane polymers:US,4482669[P].1984-11-13:1-13. |
[10] | Kaplow R.Surface modification in control SiO2 fiber fracture,ADA-108796[R].1981:8-9. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%