为了对含面芯层间脱胶缺陷的蜂窝夹芯板在侧向压缩载荷作用下的典型破坏模式进行数值预报,建立了基于蔡-希尔破坏准则和粘结模型的计算模型.该计算模型是建立在对蜂窝夹芯板的双悬臂梁(DCB)和单臂梁(SLB)试验中所发现的一种新的破坏模式的分析基础之上的.对蜂窝夹芯板的侧向压缩破坏行为的数值预报中,发现一种新的破坏模式:位于脱胶区域的面板首先发生局部屈曲失稳,随后面板内部靠近芯子的45°/0°层间出现分层,与此同时最靠近芯子的45°铺层发生断裂,伴随着45°/0°层间分层的扩展,面板发展成为对称性整体屈曲失稳.与侧向压缩试验测试结果对比发现,计算模型模拟中所预报的破坏模式在实验测试中也得到了很好的验证.
参考文献
| [1] | Goswami S,Becker W.The effect of facesheet/core delamination in sandwich structures under transverse loading[J].Composites Structures,2001,54:515-521. |
| [2] | 梁森,陈花玲,梁天锡.圆柱形胞元蜂窝夹芯板梁理论的研究[J].复合材料学报,2005,22(2):137-142.Liang Shen,Chen Hualing,Liang Tianxi.Theory of sandwich plate and beam for a circular cell honeycomb[J].Acta Materiae Compositae Sinica,2005,22(2):137-142. |
| [3] | 唐羽烨,薛明德.蜂窝夹芯板德热学与力学分析[J].复合材料学报,2005,22(2):130-136.Tang Yuye,Xue Mingde.Thermo-mechanical characteristics analysis of sandwich panel with honeycomb core[J].Acta Materiae Compositae Siniea,2005,22(2):130-136. |
| [4] | 程小全,寇长河,郦正能.复合材料夹芯板低速冲击后弯曲及横向静压特性[J].复合材料学报,2000,17(2):114-118.Cheng Xiaoquan,Kou Changhe,Li Zhengneng.Behavior of bending after low velocity impact and quasi-static transverse indentation of composite honeycomb core sandwich panels[J].Acta Materiae Compositae Sinica,2000,17(2):114-118. |
| [5] | Paik J K,Thayamballi A K,Kim G S.The strength characteristics of aluminum honeycomb sandwich panels[J].Thinwalled Structures,1999,35:205-231. |
| [6] | Gdoutos E E,Daniel I M,Wang K A.Compression facing wrinkling of composite sandwich structures[J].Mechanics of Materials,2003,35:511-522. |
| [7] | Kwon Y W,Yoon S H,Sistare P J.Compressive failure of carbon-foam sandwich composites with holes and/or partial delamination[J].Composites Structures,1997,38:573-580. |
| [8] | Vadakke V,Carlsson L A.Experimental investigation of compression failure of sandwich specimens with face/core debond[J].Composites Part B,2004,35:583-590. |
| [9] | 陈陆平,潘敬哲,钱令希.复合材料纤维/基体界面失效问题的参变量有限元数值模拟[J].复合材料学报,1993,10(1):71-75.Chen Luping,Pan Jingzhe,Qian Lingxi.The quasi parametric finite process at fibre matrix interface of composite[J].Acta Materiae Compositae Sinica,1993,10(1):71-75. |
| [10] | 叶碧泉,羿旭明,靳胜勇,梁芝茹.用界面单元法分析复合材料分析复合材料界面力学性能[J].应用数学和力学,1996,17(4):343-348.Ye Biquan,Yi Xuming,Jin Shengyong,Liang Zhiru.Analysis of interphase mechanical behavior with interface element in the composite materials[J].Appl Math Mech,1996,17(4):343-348. |
| [11] | Needleman A.A continuum model for void nucleation by inclusion debonding[J].J Appl Mech,1987,54:525-531. |
| [12] | 周储伟,杨卫,方岱宁.内聚力界面单元与复合材料的界面损伤分析[J].力学学报,1999,31(3):372-376.Zhou Chuwei,Yang Wei,Fang Daining.Cohesive interface element and interfacial damage analysis of composites[J].Acta Mechanica Sinica,1999,31(3):372-376. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%