用反应蒸发法制备了多晶V2O5薄膜,采用两电极从锂离子电解质向V2O5薄膜注入锂离子,测试了离子注入前后薄膜的红外反射光谱.实验结果表明.锂离子注入对V2O5晶体红外振动影响较大.采用多晶V2O5振动模型分析了薄膜的红外振动吸收,并得到了锂离子注入产生的V2O5薄膜振动的变化是由于晶格扩展和钒离子自身杂质形成引起的.
参考文献
| [1] | B.Pecquenard, D.Gourier, N.Baffier, Solid State Ionics, 78, 287(1995) |
| [2] | 吴广明,吴永刚,倪星元,周箴,张慧琴,金哲民,吴翔,无机材料学报,12(4),545(1997) |
| [3] | C.G.Granqvist, A.Azens, J.Isidorsson, M.Kharrazi, L.Kullman, T.Lindstreom, G.A.Niklasson, C.G.Ribbing,D.Reonnow, M.Stromme Mattson, M.Veszalei., Journal of Non-Crystalline Solids, 218, 273(1997) |
| [4] | J.M.Cocciantelli, J.P. Doumerc, M.Pouchard, M.Brousselly, J.Labat, J.Power Source, 34, 103(1991) |
| [5] | Y.Fujita, K.Miyazaki, C.Tatsuyama, Jpn. J.Appl. Phys., 24, 1082(1985) |
| [6] | M.Benmoussa, E.Ibnouelghazi, A.Bennouna, E.L.Ameziane, Thin Solid Films, 265, 22-28(1995) |
| [7] | Y.Shimizu, K.Nagase, N.Miura, N.Yamazoe, Solid State Ionics, 53～56, 490(1992) |
| [8] | A.Talledo, C.G.Granqvist, Appl. Phys., 77(9), 4655(1995) |
| [9] | L.Abello, E.Husson, Y.Repelin, G.Lucazeau, Spectrochimica Acta., 39A(7), 641(1983) |
| [10] | H.G.Bachmann, F.R.Ahmed, W.H.Barnes, Zeitschrift fur Kristallographie, Bd115, S.110-131(1961) |
| [11] | T.R.Gilson, O.F.Bizri, N.Cheetham, J.Chem. Soc. Dalton, 291(1973) |
| [12] | 梁映秋,赵文运编,分子振动和振动光谱(北京,北京大学出版社,1990)p.24 |
| [13] | 吴广明,吴永刚,吴广明,吴永刚,倪星元,周箴,张慧琴,吴翔,功能材料,30(4),404(1999) |
| [14] | 吴广明,吴永刚,倪星元,周箴,张慧琴,吴翔,陈炎,光学学报,19(5),640(1999) |
| [15] | V.Dimitrov, Y.Dimitriev, A.Montenero, J. Non-Crys. Solid, 180, 51(1994) |
| [16] | M.Primet, P. Fouilloux, B.Imelik, Surface Sci., 85, 4547(1979) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%