研究了Co68Fe7Nb5Si12B8和Co64Fe11Nb5Si12B8两种非晶合金在400～580℃温度间等温退火1h后的纳米晶化行为和磁性结果表明,在450～560℃退火1h后,在两种非晶合金的基体上均析出了单一晶相bcc结构的α-Fe(Co)固溶体.当退火温度(Ta)低于470℃时,合金具有很好的软磁性能;Ta为540～560℃,矫顽力明显增加,在弱场下磁化强度变得很低;当Ta≥580℃时,新的晶化相Co--B,Fe-B及其它化合物析出,磁性变得比较软这可能是由于具有bcc结构的α-Fe(Co)相具有大的磁致伸缩.
参考文献
| [1] | Y.Yoshizawa, S.Oguma, K.Yamauchi, J.Appl. Phys., 64, 6044(1988) |
| [2] | 赵玉华,何开元,赵恒和,张玉梅,李国纲,程力智,金属学报,36(3),291(2000)(ZHAO Yuhua, HE Kaiyan, ZHAO Henghe, ZHANG Yumei, LI Guogang, CHENG Lizhi, Acta Metaallurgica Sinica, 36(3), 291(2000)) |
| [3] | A.Serebryakov, L.Voropaeva, Yu. Levin, N.Novokhatskaya, G.Abrosimova, Nanostructured Materials, 4(7),851(1994) |
| [4] | A.Serebryakov, V.Stelmukh, A.Gurov, N.Novokhatskaya, Nanostructured Materials, 5(4), 481(1995) |
| [5] | A.Serebryakov, V.Sedykh, V.Stelmukh, N.Novokhatskaya, Nanostructured Materials, 7(5), 519(1996) |
| [6] | S.L.He, K.Y.He, B.G.Shen, J.Appl. Phys., 86(11), 6301(1999) |
| [7] | S.L.He, K.Y.He, Z.Wang, L.Z.Cheng, Y.J.Fu, Chin. Phys. Lett., 14(6), 464(1997) |
| [8] | M.L.Sui, F.Zhou, K.Y.He, R.Wang, L.Z.Cheng, Nanostructured Materials, 4(6), 734(1994) |
| [9] | R.M.Bozorth, Ferro-magnetism (New York: Van Nostrand, 1951) p.192 |
| [10] | .Y.Yoshizawa, K.Yamauchi, Mater. Sci. Eng., A133, 176(1991) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%