借助Tanaka用一维形核动力学方程导出的指数形式的相变分数,建立了一个新的形状记忆合金本构模型.提出在不同相变条件下可恢复形状记忆应变的表达式,考虑了材料在变形过程中马氏体的择优取向作用,克服了Tanaka系列模型不能描述材料处于完全马氏体状态时的力学行为的缺点.本模型比现有的形状记忆合金本构模型简单,其正确性已得到实验的检验.
参考文献
| [1] | K.Tanaka,Res Mechanica,18,251(1986) |
| [2] | Y.Sato,K.Tanaka,Res Mechanica,23,381(1988) |
| [3] | C.Liang,C.A.Rogers,Journal ofIntelligent Material Systems and Structures,1,207(1990) |
| [4] | L.C.Brison,R.Lammering,Internationaljournal of Solids and Structures,30(23),3261(1993) |
| [5] | 王健,沈亚鹏,王社良,上海力学,19(3),185(1998)(WANG Jian,SHEN Yapeng,WANG Sheliang,Shanghai Mechanics,19(3),185(1998)) |
| [6] | J.G.Boyd,D.C.Lagoudas,Journal ofIntelligent Material Systems and Structures,5,333(1994) |
| [7] | J.Hill,Mech Phys.Solids,13,213(1965) |
| [8] | C.L.Magee,The Nucleation of Martensite,Phase Transformations.edited by American Society for Metals(London,Metals Park,1970)p.115 |
| [9] | V.Birman,D.A.Hopkins,AIAA Journal,34(9),1905(1996) |
| [10] | 王健,沈亚鹏,SMA短纤维增强复合材料在热载下的相变特性,力学学报,32(2),180(2000)(WANG Jian,Shen Yapeng,Acta Mechanica Sinica,32(2),180(2000)) |
| [11] | C.M.Wayman,T.W.Duerig,An Introduction to Martensite and Shape Memory,edited by T.W.Duerig, K.N.Melton,D.Stockel,C.M.Wayman,(London,Butterworth Heinemann Ltd.,1990)p.3 |
| [12] | K.Hamada,J.H.Lee,K.Mizuuchi,M.Taya,K.Inoue,Metallurgical and Materials Transaction A,29,1127(1998) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%