选用Vectra A950热致液晶共聚酯(LCP)制备热致液晶共聚酯(LCP)/聚酰胺6(PA6)/苯乙烯-马来酸酐无规共聚物(RSMA)三元共混物,并注射成型制得复合板材,研究三元LCP/PA6/RSMA原位复合材料的形态结构、力学性质和破坏行为结果表明,RSMA是LCP/PA6复合材料的有效增容剂,RSMA的加入有利于LCP在PA6基体中原位成纤,增强了两相之间的界面粘接.加入RSMA后,LCP/PA6原位复合材料的杨氏模量、抗拉强度和抗冲击强度明显提高,RSMA能延长LCP/PA6复合材料的裂纹引发时间,增加裂纹引发能和总冲击能,对LCP/PA6原位复合材料有增韧作用.RSMA的加入量存在一临界值。
参考文献
| [1] | G.Kiss, Polym. Eng. Sci,. 27, 410(1987) |
| [2] | S.Yongsok, J.Appl. Polym.Sci., 64, 359(1997) |
| [3] | F.P. La Mantia, A.Valenza, M.Paci, P.L.Magagnini, Polym. Eng. Sci., 30, 7(1990) |
| [4] | L.Carpaneto, G.Lesage, R.Pisino, V.Trefiletti, Polymer, 40, 1781(1999) |
| [5] | R.K.Y.Li, S.C.Tjong, Xie X.L., J.Polym. Sci., Polym. Phys., 38, 403(2000) |
| [6] | X.L.Xie, S.C.Tjong, R.K.Y.Li, J.Appl. Polym. Sci., 77, 1975(2000) |
| [7] | S.C.Tjong, Y.Z.Meng, Polymer, 38, 4609(1997) |
| [8] | M.J.Sullivan, R.A.Weiss, Polym. Eng. Sci., 32, 517(1992) |
| [9] | D.Dutta, R.A.Weiss, J.He, Polymer, 37, 429(1996) |
| [10] | 解孝林,S.C.Tjong, R.K.Y.Li,材料研究学报,15(3),348(2001)XIE Xiaolin, S.C.Tjong, R.K.Y.Li, Chinese J.Mater.Research, 15(3), 348(2001) |
| [11] | N.J.Mills, P.S.Zhang, J.Mater. Sci., 24, 2099(1989) |
| [12] | G.Aggag, K.Takahashi, Polym. Eng. Sci., 36, 2260(1996) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%