通过DSC及回复应变的测量,研究了定应变约束态加热-冷却过程对预应变T州i形状酣己合金相变行为的影响结果表明,在约束态相变中,逆相变温度区间拓宽;取向马氏体除向母相转变外,应变还要进一步增大;在正相变过程中,从母相生成的马氏体也具有变形结构约束态不完全相变后,样品中存在两种马氏体:再变形马氏体和继承变形马氏体在随后的无约束逆相变过程中,前者的相变温度高于后者,并且输出两段回复应变
参考文献
| [1] | T.W.Duerig, D.Stockel, A.Keeley, in Engineering Aspects of Shape Memory Alloys, edited by T.W.Duerig,K.N.Melton, D.StSckel, C.M.Wayman, Butterworth-Heinemann Ltd. Press, London (1990) p.181 |
| [2] | D.Z.Yang, Materials and Design, 21, 503(2000) |
| [3] | Y.J.Zheng, L.SCui, D.Zhu, D.Z.Yang, Mater. Lett., 43, 91(2000) |
| [4] | A.K.Maji, Member, ASCE, I.Negret, J.Engng. Mech., 124, 1121(1998) |
| [5] | M.Piao, K.Otsuka, S.Miyazaki, H.Horikawa, Mater.Trans. JIM, 34, 919(1993) |
| [6] | Y.J.Zheng, L.S.Cui, F.Zhang, D.Z.Yang, J.Mater. Sci.Technol, 16(6), 611(2000) |
| [7] | H.Tubushi, Y.Ohashi, H.Saida, T.Hori, S.Shirai, JSME International Journal Series 1(35), 81(1992) |
| [8] | Y.Liu, Mater. Sci. Engng., A273, 668(1999) |
| [9] | H.C.Lin, S.K.Wu, T.S.Shou, H.P. Kao, Acta Metall. Mater., 39, 2069(1991) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%