通过对镍基单晶合金高温氧化后的组织结构观察和内氧化层深与循环氧化质量变化动力学曲线的测定.研究了合金的高温氧化特性.结果表明:在大气环境条件下.无保护涂层合金发生明显的氧化和内氧化:在近异形大颗粒内氧化物处出现贫Al区.使区内γ′强化相消失:内氧化层的深度随时间的变化服从抛物线规律.外加拉伸应力使内氧化加剧.在循环氧化初期.由于形成以Al为主的氧化膜易剥落.质量变化动力学曲线表现出较快的减重趋势:合金在20～80 h的循环氧化期间.在1040 C和1070℃分别呈较缓的增、减重趋势.
参考文献
| [1] | A..M.Huntz, A.Boumaza. G.Moulin. Inprovement of the Oxidation Resistance of Superalloys by Low Pressure. Plasma Sprayed MCPAIYTa Coating I. Oxid. Met.. 30, 141(1988) |
| [2] | M.Gobel. A.Rahmel, M.Schutze. The Iosthermal Oxidation Behavior of Several Nickel Base Single Crystal Superalloys with and Without Coatings. Oxid. Met.. 39(3/4). 231(1993) |
| [3] | M.Levy. R.Huie, Pettit. Oxidation of Some Advanced Single Crystal Nickel- Base Superalloys in Air at 2000 F (1093 C). Corrosion. 42. 708(1986) |
| [4] | M. Levy. R. Huie. F.Pettit. Oxidation and Hot Corrosion of Some Advanced Superalloys at 1300 to 2000°F(704 to 1093 C). Corrosion. 45. 661(1989) |
| [5] | B.Pieraggi, F.Dabosi. High-Temperature Oxidation of A Single Crystal Ni Base Superalloy. Werkst. Norrhs38, 584(1987) |
| [6] | F.H.Stott. G.C.Wood. Internal Oxidation, Mater. Sci and Tech.. 4. 1072(1988) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%