研究了可交联硅烷接枝聚乙烯共混物(PEBX)的熔体流动速率(MFR),维卡软化点测试过程中的温度变形关系,拉伸性能及结晶行为等性质.研究结果表明:(I)纯聚乙烯共混物(PEB)的MFR基本上不随时间变化,而PEBX的MFR随时间减小;(Ⅱ)在相同的温度下,交联后的聚乙烯共混物(CPEBX)的变形量小于PEB和PEBX,而PEBX又小于PEB,在维卡软化点附近的温度,CPEBX的变形速率远小于PEB和PEBX;(Ⅲ)CPEBX有交联,但其断裂伸长率与PEBX和PEB的相近,未受到交联的影响,其屈服应力高于PEBX和PEB;(Ⅳ)CPEBX的熔点和熔程与PEBX及PEB的差不多,但结晶度比后两者的有所升高.讨论了产生上述特性的原因.
参考文献
| [1] | A.K.Sen,B.Mukherjee,A.S.Bhattacharyya,P.P.De,A.K.Bhowmick,J.Appl.Polym.Sci.,44,1153(1986) |
| [2] | A.K.Sen,B.Mukherjee,A.S.Bhattacharyya,P.P.De,A.K.Bhowmick,J.Therm.Anal.,39,887(1993) |
| [3] | Y.H.Koo,P.J.Phillips,Polymer,27,1669(1986) |
| [4] | D.J.Bullen,G.Capaccio,C.J.Frye,Br.Polym.J.,21,117(1989) |
| [5] | M.Palmlof,T.Hjertberg,B.A.Sultan,J.Appl.Polym.Sci.,42,1193(1985) |
| [6] | Vlren,T.Hjertberg,J.Adhesion,31,117(1990) |
| [7] | M.Narkis,A.Vaxman Tzur,Polym.Eng.Sci.,25,857(1985) |
| [8] | Y.T.Shieh,T.H.Tsai,J.Appl.Polym.Sci.,69,255(1998) |
| [9] | M.Beltran,C.Mijangos,Polym.Eng.Sci.,40,1534(2000) |
| [10] | N.C.Liu,G.P.Yao,H.Huang,Polymer,41,4537(2000) |
| [11] | Li Zhongming(李忠明),Yang Mingbo(杨鸣波),Feng Jianmin(冯建民),Huang Rui(黄锐),PlasticsIndustry(塑料工业),27(6),1(1999) |
| [12] | B.Wunderlich,Macromolecular Physics,Vol.3 (New York,Academic Press,1980) p.375 |
| [13] | Wang Shanqi(王善琦),Macromolecular Chemistry(高分子化学)(Xi'an(西安),North-West Polytechnitic University Press(西北工业大学出版社),1991)p49 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%