分析了螺旋炭纤维的微观结构,发现其主要由纳米级石墨片层(nano graphite structurecell,NGSC,约为5 nm×5 nm)构成,其间夹杂着无定形碳和多层富勒烯等无序结构.由于螺旋炭纤维具有螺旋结构,其中的NGSC发生了一定的弯曲.在宏观尺度上,螺旋炭纤维表现出无序碳结构的特征.根据结构分析的结果提出了表征螺旋炭纤维的几何参数,并对不同螺旋炭纤维的螺旋角进行了比较分析.结果表明,虽然螺旋炭纤维的直径和螺距各不相同,但是其螺旋角具有一定的规律.在微观结构观察和几何构形分析的基础上提出了螺旋炭纤维的生长机理.
参考文献
| [1] | S.Motojima, M.Kawaguchi, K.Nozaki, Carbon, 29(3), 379(1991) |
| [2] | X.Q.Chen, S.M.Yang, S.Motojima, Materials Letters, 3751(2002) |
| [3] | K.Shibagaki, S.Motojima, Carbon, 39, 411(2001) |
| [4] | X.Q.Chen, S.Motojima, H.Iwanga, J. Crys. Grow., 237～279, 1931(2002) |
| [5] | C.Kuzuya, Y.hayashi, S.Motojima, Carbon, 40, 1071(2002) |
| [6] | X.Q.Chen, T.Saito, M.Kusunoki, S.Motojima, J. Mater. Res., 14(11), 4329(1999) |
| [7] | S.Motojima, X.Q.Chen, J. Appl. Phys., 85(7), 3919(1999) |
| [8] | X.Q.Chen, S.Motojima, Carbon, 37, 1817(1999) |
| [9] | W.In-Hwang, X.Q.Chen, T.Kuzuya, K.Kawabe, S.Motojima, Carbon, 38, 565(2000) |
| [10] | S.Motojima, Y.Itoh, S.Asakuba, H.Iwanaga, J. Mater. Sci., 30, 5049(1995) |
| [11] | K.Kaneto, M.Tsuruta, S.Motojima, Synthetic Metals, 103, 2578(1999) |
| [12] | Du Jinhong, Su Ge, Bai Shuo, Sun Chao, Cheng Huiming, Science in China (series E), 44(4), 376(2001) |
| [13] | SU Ge, DU Jinhong, FAN Yueying, CHENG Huiming, Chinese Journal of Materials Research, 15(6),623(2001)(苏革,杜金红,范月英,成会明,材料研究学报,15(6),623(2001)) |
| [14] | Du Jinhong, Electromagnetic Properties and Microwave Absorption Characteristics of Fibrous Nano-Carbon Materials and their Composites, Ph.D Thesis, Institute of Metal Research, Chinese Academy of Sciences,Shenyang, 2003(杜金红,纤维状纳米炭及其复合材料的电磁性能与微波吸收特性研究(博士论文),中国科学院金属研究所,沈阳,2003) |
| [15] | Cheng Huiming, Carbon Nanotube-Synthesis, Microstructure, Properties and Applications (Beijing, Chemical Industry Press, 2002) p.446(成会明,纳米碳管-制奋、结构、物性及应用(北京,化学工业出版社,2002)p.446) |
| [16] | Tan Pingheng, Raman Scattering of Single-Walled Carbon Nanotube and its Related Materials, Ph.D Thesis,Institute of Semiconductors, Chinese Academy of Sciences, Beijing 2001(潭平恒,碳纳米管及其相关材料的Raman光谱学研究(博士论文),中国科学院半导体研究所,北京,2001) |
| [17] | P.L.Walker, Jr(ed.), Chemistry and Physics of Carbon, Volume 5, Marcel Dekker, (1969) p.9 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%