制备了高频MnZn功率铁氧体,研究了添加CaO和V2O5对高频MnZn铁氧体性能的影响.结果表明:对于工作频率高于500 kHz的MnZn功率铁氧体,增加CaO的添加量,可提高晶界电阻率,最大程度地降低涡流损耗;适当添加V2O5会形成液相烧结并使晶粒细化,增加晶界,减少晶粒和晶界内的气孔率,提高晶界电阻率,降低材料的损耗.添加0.3%CaO和0.1%V2O5(质量分数,下同),可以制备出致密、气孔率低和晶粒均匀(粒径3～5 μm)的高频功率铁氧体材料,其起始磁导率约为1500,磁芯损耗约为130 mW/cm3(500 kHz,50 mT,25℃).
参考文献
| [1] | WANG Gan, DAI Jingying, WANG Youjun, J. Magn. Mater. Device, 26(2), 40 (1995)(汪敢,戴京营,王友军,磁性材料及器件,26(2),40(1995)) |
| [2] | LI Haihua, FENG Zekun, HE Huahui, Instrument Technique and Sensor, (4), 10(2001)(李海华,冯则坤,何华辉,仪表技术与传感器,(4),10(2001)) |
| [3] | S.Gasiorck, J.Kulikowski, J. Mang. Magn. Mater., 26, 295(1982) |
| [4] | A.Akashi, Trans. Jpn. Inst. Mat., 2, 171(1961) |
| [5] | A.Znidarsic, M.Limpel, M.Drofenik, IEEE Trans. on Magn., 31(2), 950(1995) |
| [6] | I-Nan Lin, R.Mishra, G.Thomas, IEEE Trans. on Magn., Mag-18(6), 1544(1982) |
| [7] | Ying-Chun Lin, Dershin Gan, Pouyan Shen, Mater. Sci. Eng., A188, 327(1994) |
| [8] | P. Andrei, O.F.Caltun, C.Papusoi, A.Stancu, M.Feder, J. Magn. Magn. Mater., 196～197, 362(1999) |
| [9] | R.J.Willey, J.T.Mullin, J. Magn. Magn. Mater., 26, 315(1982) |
| [10] | H.Tsunekawa, A.Nakata, T.Kamijo, K.Okutani, R.K.Mishra, G.Thomas, IEEE Trans on Magn., MAG15(6), 1855(1979) |
| [11] | C.S.Liu, J.M.Wu, M.T.Tsay, C.J.Chen, IEEE Trans. on Magn., 32(5), 4860(1996) |
| [12] | Geun-Min Jeong, Jaeho Choi, Sung-Soo Kim, IEEE Trans. on Magn., 36(5), 3405(2000) |
| [13] | G.C.Jain, B.K.Das, S.Kumari, IEEE Trans. on Magn., MAG-16(6), 1428(1980) |
| [14] | O.Inoue, N.Maysutani, K.Kugimiya, ICF, 6, 1155(1992) |
| [15] | S.Yamada, E.Qtsuki, J. Appl. Phys, 81, 4791(1997) |
| [16] | H.Rikukawa, IEEE Trans. on Magn., 18(6), 1535(1982) |
| [17] | S.Otobe, Y.Yachi, T.Hashimoto, T.Tanimori, T.Shigenaga, H.Takei, K.Hontani, IEEE Trans. on Magn.,35(5), 3409(1999) |
| [18] | Y.Matsuo, K.Ono, T.Hashimoto, F.Nakao, IEEE Trans. on Magn., 37(4), 2369(2001) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%