用磁控溅射法制备了掺杂Sn的Ge2Sb2Te5相变材料薄膜,研究了Sn含量对结晶性能的影响.薄膜的X射线衍射(XRD)表明,热处理使薄膜发生了从非晶态到晶态的相变,并出现Sn-Te相.通过示差扫描量热(DSC)实验测出在不同加热速率下非晶态薄膜粉末的结晶峰温度,计算了材料的结晶活化能.根据结晶动力学分析和结晶活化能数据,掺杂Sn后的Ge-Sb-Te具有更高的结晶速率,用于光存储时将具有更高的擦除速度.
参考文献
| [1] | J.Feinleib, S.R.Ovshinsky, J.Non-Crystalline Solids, 4, 564(1970) |
| [2] | Myong R. Kim, Hun Seo, Tae H. Jung, Proc. SPIE., 3401, 259(1998) |
| [3] | Chain-Ming Lee, Tsung-Shune Chin, Yi-Yuan Huang, Jpn. J. Appl. Phys, 39(11), 6369(2000) |
| [4] | GU Sipeng, HOU Lisong, LIU Bo, Acta Optica Sinica, 22(9), 1137(2002)(顾四朋,侯立松,刘波,光学学报,22(9),1137(2002)) |
| [5] | GU Sipeng, HOU Lisong, J. Inorg. Mater., 17(6), 1258(2002)(顾四朋,侯立松,无机材料学报,17(6),1258(2002)) |
| [6] | GU Sipeng, HOU Lisong, ZHAO Qitao, HUANG Ruian, Acta Optica Sinica(in press)(顾四朋,侯立松,赵启涛,黄瑞安,光学学报,待发表) |
| [7] | Hu Hefang, Lin Fengying, Yuan Yibo, J. Non-Cryst. Solids, 112, 306(1989) |
| [8] | H.Yinno, D.R.Uhlmann, J. Non-Cryst. Solids, 54, 253(1983) |
| [9] | Xiujian Zhao, Liangying Xu, Hongling Yin, J. Non-Cryst. Solids, 167, 70(1994) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%