用溶胶-凝胶法制备了不同空位浓度掺杂的La0.67-xCa0.33MnO3系列样品(x=0.00,0.02,0.06,0.10),用扫描电子显微镜(SEM)观察了样品的形态和颗粒大小,X射线衍射实验结果显示样品为单相钙钛矿结构,用振动样品磁强计(VSM)测量了样品的磁化强度随温度变化的M-T曲线和起始磁化M-H曲线.研究了空位浓度对样品的居里温度Tc和磁熵变的影响.结果表明,空位浓度的掺杂将样品的居里温度Tc提高至室温附近,磁熵变得到增强.对于经历了一级相变的样品La0.67-xCa0 33MnO3(x=0.02),在居里温度Tc(277 K)附近和1T外磁场下,最大磁熵变达到了2.78 J/(kg·K).
参考文献
| [1] | V.K.Pecharsky, K.A.Gschneidner, Appl. Phys. Lett., 70(24), 3299(1997) |
| [2] | Z.B.Guo, Y.W.Du, J.S.Zhu, H.Huang, W.P. Ding, D.Feng, Phys. Rev. Lett., 78, 1142(1997) |
| [3] | M.H.Phan, S.B.Tian, D.Q.Hoang, S.C.Yu, C.Nguyen, A.N.Ulyanov, J. Magn. Magn. Mater., 258～259,309(2003) |
| [4] | X.X.Zhang, J.Tejada, Y.Xin, G.F.Sun, K.W.Wong, X.Bohigas, Appl. Phys. Lett., 69(23), 3596(1996) |
| [5] | H.Huang, Z.B.Guo, D.H.Wang, Y.W.Du, J. Magn. Magn. Mater., 173,302(1997) |
| [6] | Z.M.Wang, G.Ni, Q.Y.Xu, H.Sang, Y.W.Du, J. Appl. Phys., 90(11), 5689(2001) |
| [7] | W.Zhong, W.Chen, W.P.Ding, N.Zhang, A.Hu, Y.W.Du, Q.J.Yan, J. Magn. Magn. Mater., 195, 112(1999) |
| [8] | P. Chen, Y.W.Du, J. Phys. D: Appl. Phys., 34, 1868(2001) |
| [9] | CHEN Wei, ZHONG Wei, PAN Chengfu, CHANG Hong, DU Youwei, Acta Physica Sinica, 50(02), 320(2001)(陈伟,钟伟,潘成福,常虹,都有为,物理学报,50(02),320(2001)) |
| [10] | Q.Y.Xu, K.M.Gu, X.L.Liang, G.Ni, Z.M.Wang, H.Sang, Y.W.Du, J. Appl. Phys., 90(1), 524(2001) |
| [11] | W.Chen, W.Zhong, D.L.Hou, R.W.Gao, W.C.Feng, M.G.Zhu, Y.W.Du, J. Phys.: Condens. Matter, 14,11889(2002) |
| [12] | M.H.Phan, S.C.Yu, N.H.Hur, J. Magn. Magn. Mater., 262, 407(2003) |
| [13] | N.H.Sinh, N.P.Thuy, J. Magn. Magn. Mater., 262, 502(2003) |
| [14] | L.E.Hueso, P. Sande, D.R. Miguéns, J.Rivas, J. Appl. Phys., 91(12), 9943(2002) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%