通过控制固化条件获得具有不同交联程度的酚醛纤维,考察其交联程度对经900℃炭化后所获炭纤维结构和性能的影响.结果表明,具有高度交联化酚醛纤维,交联程度低的分子相对较少,热解过程中低分子逸出量少,形成的孔道也相对较少,参与交联缩合的分子相对较多,有利于六方晶系炭的形成.由此导致适当温度下炭化所获炭纤维炭化收率高、孔容小、机械拉伸强度和电导率相应较高.
参考文献
| [1] | M.H.Choi,B.H.Jeon,I.J.Chung,Polymer,41,3243(2000) |
| [2] | D.M.Bigg,Polym Engng.Sci.,19,1188(1979) |
| [3] | P.B.Jana,A.K.Mallick,S.K.De,Polym Compos.,22,1(1991) |
| [4] | E.Fitzer,W.Schafer,S.Yamada,Carbon,7,643(1969) |
| [5] | H.A.Mackay,Carbon,8,517(1970) |
| [6] | E.Fitzer,W.Schafer,Carbon,8,353(1970) |
| [7] | C.L.Liu,Q.G.Quo,J.L.Shi,L.Liu,Materials Chemistry and Physics,90,315(2005) |
| [8] | M.Kruk,M.Jaroniec,Y.Bereznitski,J.Colloid Interface Sci.,182(1),282(1996) |
| [9] | J.I.Ozaki,W.Ohizumi,A.Oya,Carbon,38,1515(2000) |
| [10] | LIU Chunling,GUO Quangui,SHI Jingli,LIU Lang,New Carbon Materials,19(2),124(2004) (刘春玲,郭全贵,史景利,刘朗,新型炭材料,19(2),124(2004)) |
| [11] | C.Z.Hu,Polymer,28,663(1987) |
| [12] | N.Kishore,S.Sachan,K.N.Rai,A.Kumar,Carbon,41,2961(2003) |
| [13] | F.Tuinstea,J.Chem.Phy.s,53,1126(1970) |
| [14] | E.Fitzer,Carbon,26,594(1988) |
| [15] | E.Fitzer,High Temperature-High Pressure,20,449(1988) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%