用溅射Fe和电沉积Fe3O4先驱体硫化制备出FeS2薄膜,研究了不同先驱体对硫化过程和FeS2薄膜性能的影响.结果表明,两种先驱体结晶成的FeS2能够在一定程度上保留先驱体形貌特征.Fe生成FeS2的热力学驱动力比较高,虽然可能生成FeS的过渡相;Fe硫化生成的薄膜平整致密,晶粒生长比较充分,尺寸较大,其禁带宽度接近理论值.Fe3O4硫化生成FeS2的热力学驱动力较低,生成的薄膜表面疏松多孔,晶粒细小;薄膜的晶界等面缺陷比例较大和几何连续性较低使其电阻率较高、禁带宽度和载流子迁移率低于Fe膜硫化FeS2薄膜.
参考文献
| [1] | J.Herrero,J.Ortega,Solar Energy Materials,17(5),357(1988) |
| [2] | N.Takahashi,T.Yatomi,T.Nakamura,Solid State Science,6,1269(2004) |
| [3] | L.Meng,Y.H.Liu,L.Tian,Materials Research Bulletin,38(6),941(2003) |
| [4] | Y.H.Liu,L.Meng,L.Zhang,Thin Solid Films,479(1-2),83(2005) |
| [5] | A.Yamamoto,M.Nakamura,A.Seki,E.L.Li,A.Hashimoto,S.Nakamura,Solar Energy Materials and Solar Cells,75,451(2003) |
| [6] | A.Gomes,J.R.Ares,I.J.Ferrer,M.I.Da Silva Pereira,C.Sánchez,Materials Research Bulletin,38(7),1123(2003) |
| [7] | L.Reijnen,B.Meester,A.Goossens,J.Schoonman,Journal of the Electrochemical Society,147(5),1803(2000) |
| [8] | G.Smestad,A.Ennaoui,S.Fiechter,H.Tributsch,W.K.Hofmann,M.Birkholz,W.Kautek,Solar Energy Materials,20(3),149(1990) |
| [9] | LIU Yanhui,MENG Liang,ZHANG Xiujuan,Chinese Journal of Materials Research,18(4),373(2004)(刘艳辉,孟亮,张秀娟,材料研究学报,18(4),373(2004)) |
| [10] | G.Pimenta,W.Kautex,Thin Solid Films,219(1),37(1992) |
| [11] | A.Ennaoui,S.Feichter,Ch.Pettenkofer,N.Alonso-Vante,K.Büker,M.Bronold,Ch.H(o)pfner,H.Tributsch,Solar Energy Materials and Solar Cells,29,289(1993) |
| [12] | C.de las Heras,V.J.L.Martin,I.J.Ferrer,C.Sánchez,Jourhal of Materials Research,11(1),211(1996) |
| [13] | J.R.Ares,A.Pascual,I.J.Ferrer,C.Sánchez,Thin Solid Films,451,233(2004) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%