测量电晕老化前后Kapton 100 HN聚酰亚胺薄膜在均匀直流电场中的电致发光强度和光谱,研究了电致发光强度与外加电场强度的关系.结果表明:聚酰亚胺薄膜的电致发光强度随着外加电场强度的提高而提高.聚酰亚胺薄膜的电致发光谱由荧光区、磷光区和红光及红外三个区域组成,电致发光的阈值场强约为2.8 MV/cm.电晕老化处理后,聚酰亚胺薄膜的电致发光阈值场强降低,光子的产率提高并出现新峰.这些结果是电晕老化效应的综合作用所导致的.
参考文献
| [1] | W.A.Hartman,H.L.Armstrong,J.Appl.Phys.,38(1),2393(1967) |
| [2] | M.Kosaki,N.Shimizu,K.Horii,IEEE Trans.EI.,12(1),40(1977) |
| [3] | D.G.Lidzey,D.D.C.Bradlley,S.F.Alvarado,P.E.Seidler,Nature,1(386),135(1997) |
| [4] | C.Laurent,IEEE Electr.Insul.Mag.,15,5(1999) |
| [5] | S.S.Bamji,IEEE Electr.Insul.Mag.,15,9(1999) |
| [6] | M.Kochi,H.Shimada,H.Kambe,J.Polym.Sci.:Polym.Phys.Ed.,22,1979(1984) |
| [7] | M.Katz,R.Theis,IEEE Electrical Insulation Magazine,13(4),24(1997) |
| [8] | D.Mary,M.Albertin,C.Laurent,J.Phys.D:Appl; phys;,UK,30,171(1997) |
| [9] | K.Iida,T.Tanimoto,S.Nakamura,G.Sawa.,IEEE Trans.On Electrical Insulation,22(4),133(1987) |
| [10] | ZHANG Peihong,LIU Yan,WANG Fochi,FAN Yong,LEI Qingquan,Journal Harbin University Sci.& Tech.,9(1),54(2004)(张沛红,刘岩,汪佛池,范勇,雷清泉,哈尔滨理工大学学报,9(1),54(2004)) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%