采用H2/N2/H2O混合气体在850℃下还原含有少量Ni/Fe/Co的氧化钨混合粉末的方法,制备出金属钨纳米针.用SEM、TEM和EDS分析等方法对金属钨纳米针进行了表征.结果表明:纳米针的顶部直径为30～70 nm,根部直径为150～200 nm,长度为2～10 μm;纳米针具有完好的BCC单晶结构,沿〈100〉方向生长;在纳米针的生长过程中Ni/Fe/Co起到了顶端催化作用.
参考文献
| [1] | E.Lassner,W.D.Schubert,Tungsten:Properties,Chemistry,Technology of the Element,Alloys and Chemical Compounds (New York,Kluwer Academic/Plenum Publishes,1998) p.7 |
| [2] | Y.H.Lee,C.H.Choi,Y.T.Jang,E.K.Kim,B.K.Ju,Appl.Phys.Lett.,81(4),745(2002) |
| [3] | D.S.Chung,W.B.Choi,J.H.Kang,H.Y.Kim,I.T.Han,I.Y.Park,Y.H.Lee,N.S.Lee,J.E.Jung,J.M.Kim,J.Vac.Sci.Technol.B,18(2),1054(2000) |
| [4] | A.G.Umnov,Y.Shiratori,H.Hiraoka,Appl.Phys.A,77(1),159(2003) |
| [5] | Y.N.Xia,P.D.Yang,Y.G.Sun,Y.Y.Wu,B.Mayers,B.Gates,Y.D.Yin,F.Kim,H.Q.Yan,Adv.Mater.,15(5),353(2003) |
| [6] | S.Vaddiraju,H.Chandrasekaran,M.K.Sunkara,J.Am.Chem.Soc.,125(36),10792(2003) |
| [7] | T.Karabacak,A.Mallikarjunan,J.P.Singh,D.Ye,G.C.Wang,T.M.Lu,Appl.Phys.Lett.,83(15),3096(2003) |
| [8] | J.T.L.Thong,C.H.Oon,M.Yeadon,W.D.Zhang,Appl.Phys.Lett.,81(25),4823(2002) |
| [9] | Z.Q.Liu,K.Mistsuishi,K.Furuya,Nanotechnology,15(6),S414(2004) |
| [10] | J.W.Wang,Y.D.Li,Adv.Mater.,15(5),445(2003) |
| [11] | O.L.Guise,J.W.Ahner,M.C.Jung,P.C.Goughnour,J.T.Yates,Jr,Nano Lett.,2(3),191(2002) |
| [12] | Y.H.He,L.B.Chen,B.Y.Huang,P.K.Liaw,Inter.J.of Refractory & Hard Metals,21(1),227(2003) |
| [13] | S.Guha,C.Kyriacou,J.Withers,R.Loutfy,Mater.Manuf.Process,9(6),1061(1994) |
| [14] | J.T.Hu,T.W.Odom,C.M.Lieber,Acc.Chem.Res.,32(5),435(1999) |
| [15] | A.I.Persson,M.W.Larsson,S.Stenstr(o)m,B.J.Ohlsson,L.Samuelson,L.R.Wallenberg,Nature Materials,3(10),677(2004) |
| [16] | K.A.Dick,K.Deppert,T.M(a)rtensson,B.Mandl,L.Samuelson,W.Seifert,Nano Lett.,5(4),761(2005) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%