用Nd:YAG脉冲激光在低硅钢表面制备激光熔覆高硅涂层,研究了激光熔覆高硅涂层样品的组织和磁性能.结果表明,制备出的激光熔覆高硅涂层组织致密、无气孔和裂纹,且与基体有良好的冶金结合.经激光熔覆后硅钢表面存在熔覆区、界面结合区和热影响区.熔覆区的显微组织不均匀,随着与结合界面距离的增加,由柱状晶变为树枝晶,最终过渡到表层的细小树枝晶组织.熔覆层与基体之间的结合界面为平面晶组织,热影响区为马氏体组织.熔覆涂层的显微硬度远高于低硅钢基体,其主要原因是涂层具有较高的Si含量,涂层中的α-Fe和γ-Fe双相组织也导致了硬度的提高.激光熔覆高硅涂层硅钢样品经扩散退火后具有室温铁磁性,Si含量的提高使其室温直流磁性能优于原始低硅钢.
参考文献
| [1] | H.Haiji,K.Okada,T.Hiratani,M.Abe,M.Ninomiya,Magnetic properties and workability of 6.5% Si steel sheet,Journal of Magnetism and Magnetic Materials,160,109(1996) |
| [2] | Y.Ushigami,M.Mizokami,M.Fujikura,T.Kubota,H.Fujii,K.Murakami,Recent development of low-loss grainoriented silicon steel,Journal of Magnetism and Magnetic Materials,254-255,307(2003) |
| [3] | F.Fiorillo,E.Ferrara,L.Ferrando,C.Appino,C.Legourg,J.Degauque,M.Baricco,Magnetic losses and mechanical properties of Fe-4 to 7.8 wt.% Si rapidly quenched alloys,IEEE Transactions on Magnetics,33(5),3802(1997) |
| [4] | YANG Lin,TIAN Chong,CHEN Guiyun,ZHANG Yongchang,YE Hengqiang,Microstructure and properties of Fe-4.5wt%Si steel produced by spay forming and rolling,Materials Science & Technology,10(1),55(2002)(杨林,田冲,陈桂云,张永昌,叶恒强,喷射轧制Fe-4.5%Si 硅钢片的组织和性能,材料科学与工艺,10(1),55(2002)) |
| [5] | K.Okada,T.Yamaji,K.Kasai,Basic investigation of CVD method for manufacturing 6.5% Si steel sheet,ISIJ International,36(6),706(1996) |
| [6] | K.Fujita,M.Namikawa,Y.Takada,Magnetic properties and workability of 6.5% Si steel sheet manufactured by siliconizing process,Journal of Materials Science & Technology,16(2),137(2000) |
| [7] | WANG Lei,WU Xinjie,LI Pingsheng,CHEN Dakai,Research on 6.5% silicon steel produced by PCVD technique,Metal Heat Treatment,(12),27(2002)(王蕾,吴新杰,李平生,陈大凯,PCVD法制高Si钢片的研究,金属热处理,(12),27(2002)) |
| [8] | I.Manna,J.D.Majumdar,B.R.Chandra,S.Nayak,N.B.Dahotre,Laser surface cladding of Fe-B-C,Fe-B-Si and Fe-BC-Si-Al-C on plain carbon steel,Surface & Coatings Technology,201,434(2006) |
| [9] | R.Jagdheesh,U.Kamachi Mudali,D.Sastikumar,A.K.Nath,Laser cladding of Si on austenitic stainless steel,Surface Engineering,21(2),113(2005) |
| [10] | W.T.Tsai,T.Hwunh Lai,J.J.Lee,Laser surface alloying of stainless steel with silicon nitride,Materials Science and Engineering,A183,239(1994) |
| [11] | GAO Yang,TONG Baiyun,LIANG Yong,Investigation on structure and properties of laser remelting Ni-base alloy coatings,Chinese Journal of Materials Research,17(1),87(2003)(高阳,佟百运,梁勇,激光熔敷Ni基合金涂层的结构与性能,材料研究学报,17(1),87(2003)) |
| [12] | J.M.Pelletier,L.Renaud,F.Fouquet,Solidification microstructures induced by laser surface alloying:influence of the substrate,Materials Science and Engineering,A134,1283(1991) |
| [13] | SONG Jianli,DENG Qilin,HU Dejin,CHEN Changyuan,Microstructure characterization and properties of laser cladding forming 316L stainless steel,Chinese Journal of Lasers,32(10),1441(2005)(宋建丽,邓琦林,胡德金,陈畅源,激光熔覆成形316L不锈钢组织的特征与性能,中国激光,32(10),1441(2005)) |
| [14] | S.Sun,Y.Durandet,M.Brandt,Parametric investigation of pulsed Nd:YAG laser cladding of satellite 6 on stainless steel,Surface & Coatings Technology,194(2～3),225(2005) |
| [15] | HAO Nanhai,LU Wei,ZUO Tiecuan,Thermalmechanical coupling finite element analysis of temperature field in laser cladding process,China Surface Engineering,(69),6(2004)(郝南海,陆伟,左铁钏,激光熔覆过程热力耦合有限元温度场分析,中国表面工程,(69),6(2004)) |
| [16] | ZHENG Jingwu,JIANG Liqiang,CHEN Qiaoling,QI Fangliang,Influence of electrodeposited conditions on magnetic performance of soft magnetic iron foil,Chinese Journal of Rare Metals,30(3),266(2006)(郑精武,姜力强,陈巧玲,齐方良,电沉积工艺参数对软磁铁箔磁性能的影响,稀有金属,30(3),266(2006)) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%