采用2024-T3铝合金含中心孔试件进行了实验室空气环境和潮湿空气环境下的疲劳寿命实验及升降法实验,研究了潮湿空气环境对2024-T3铝合金疲劳性能的影响.结果表明,潮湿空气环境显著降低了2024-T3铝合金的疲劳性能,潮湿空气环境对其疲劳寿命特征值和疲劳强度均值的影响系数分别为0.6059和0.8722;在潮湿空气环境中疲劳寿命的分散性变大,用疲劳寿命的中值或特征值得到的腐蚀影响系数进行可靠度95%的腐蚀环境下的寿命修正,将得到偏危险的结果.用潮湿空气环境对基本可靠性寿命的影响系数由标准S-N曲线折算得到的对疲劳强度的影响系数与升降法测得的对疲劳强度的影响系数基本一致,在潮湿空气环境下标准S-N曲线参数仍然适用.
参考文献
| [1] | Robert P.Wei,Corrosion and Corrosion Fatigue of Airframe Materials,DOT/FAA/AR-00/22,2000. |
| [2] | JIANG Zuguo,Corrosion Fatigue for Aircraft Structures (Beijing,Aviation Industry Press,1992) p.39(蒋祖国,飞机结构腐蚀疲劳(北京,航空工业出版社,1992)p.39) |
| [3] | J.E.Zamber,B.M.Hillberry,A Probabilistic Approach to Predicting Fatigue Lives of Corroded 2024-T3,AIAA-98-2054 |
| [4] | Ruoxue Zhang,Sankaran Mahadevan,Reliability-based reassessment of corrosion fatigue life,Structural Safty,23,77～91(2001) |
| [5] | R.S.Piascik,S.A.Willard,The growth of small corrosion fatigue cracks in alloy 2024,Fatigue and Fracture of Engineering Materials & Structures,17,1247～1259(1994) |
| [6] | A.D.B.Gingell,J.E.King,The effect of frequency and microstructure on corrosion fatigue crack propagation in high strength aluminum alloys,Acta Mater.,45(9),3855～3870(1997) |
| [7] | ZHENG Xiaoling,LI Lingfang,Handbook of Civil Aircraft Structures Durability and Damage Tolerance Design (Beijing,Aviation Industry Press,2003) p.288(郑晓玲主编,民机结构耐久性与损伤容限设计手册(北京,航空工业出版社,2003)p.288) |
| [8] | BAO Rui,ZHANG Jianyu,CHEN Bo,FEI Binjun,The up and down method for DFR testing,Journal of Beijing University of Aeronautics and Astronautics,30(1),47(2004)(鲍蕊,张建宇,陈勃,费斌军,试验测定DFR的升降法方法,北京航空航天大学学报,30(1),47(2004)) |
| [9] | ZHANG Jianyu,BAO Rui,CHEN Bo,FEI Binjun,Study on DFR method under corrosive environment for fatigue analysis,Journal of Beijing University of Aeronautics and Astronautics,30(6),547(2004)(张建宇,鲍蕊,陈勃,费斌军,腐蚀环境下疲劳分析的DFR方法研究,北京航空航天大学学报,30(6),547(2004)) |
| [10] | GAO Zhentong,Statistics in Fatigue (Beijing,National Defense Industry Press,1986) p.336(高镇同,疲劳应用统计学[M](北京,国防工业出版社,1986)p.336) |
| [11] | D.V.Ramsamooj,T.A.Shugar,Modeling of corrosion fatigue in metals in an aggressive environment,International Journal of Fatigue,23,S301-S309(2001) |
| [12] | LIU Wenting,YANG Hongyuan,HE Xiaofan,Journal of Beijing University of Aeronautics and Astronautics,8,753(2004)(刘文廷,杨洪源,贺小帆,北京航空航天大学学报,8,753(2004)) |
| [13] | M.L.Du,F.P.Chiang,Damage of Al 2024 alloy due to sequential exposure to fatigue,corrosion and fatigue,Int.J.fatigue,20(10),743(1998) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%