铸态GH742合金中存在复杂的第二相组织和严重的枝晶偏析,Nb,Ti大量富集于枝晶间和MC碳化物、Laves 相,δ相,(γ+γ')等析出相中.本文确定了γ基体的熔化温度为1160℃,并通过不同的均匀化处理确定了γ'相,(γ+γ')共晶、MC碳化物、Laves相、δ相、Ni5Ce相及含氧硫稀土相等析出相的溶解温度.由于稀土相在1120℃发生熔化,提出一种GH742合金低温预处理加高温扩散的二次均匀化制度来扩大其均匀化温度区间,提高扩散退火温度,从而获得均一的组织.元素扩散计算结果表明,提高均匀化温度可以提高元素的扩散系数;Nb的偏析系数比Ti的小得多,达到完全均匀化需要很长的时间.
参考文献
| [1] | L.Zheng,C.Q.Gu,Y.R.Zheng,Investigation of the solidification behavior of a new Ru-containing cast Ni-base superalloy with high W content,Scripta Materialia,50,435(2004) |
| [2] | J.N.Dupont,C.V.Robino,J.R.Michael,M.R.Notis,A.R.Marder.Solidification of Nb-bearing superalloys:part I.reaction sequences,Metallurgical and Materials Transactions A,29,2785(1998) |
| [3] | W.R.Sun,S.R.GUO,D.Z.Lu,Z.Q.Hu,Effect of sulfur on the solidification and segregation in Inconel 718 alloy,Materials Letters,31,195(1997) |
| [4] | S.L.Semiatin,R.C.Kramb,R.E.Turner,F.Zhang,M.M.Antony,Analysis of the homogenization of a nickel-base superalloy,Scripta Materialia,51,491(2004) |
| [5] | R.C.Kramb,M.M.Antony,S.L.Semiatin,Homogenization of a nickel-base superalioy ingot material,Scripta Materialia,54,1645(2006) |
| [6] | XIE Yongjun,LIANG Xuefeng,MIU Hongbo,LI Wei,Microstructure and segregation elimination of superalloy GH742 ingot,Journal of Iron and Steel Research,15(7),17(2003)(谢永军,梁学锋,缪宏博,李伟,GH742合金钢锭的组织及偏析的消除,钢铁研究学报,15(7),17(2003)) |
| [7] | TIAN Yuliang,WANG Ling,DONG Jianxin,ZHANG Maicang,Microeegregation of GH742 ingot and the element distribution during homogenizing treatment,Rare Metal Materials and Engineering,35(8),1315(2006)(田玉亮,王玲,董建新,张麦仓,GH742铸锭偏析及均匀化过程中元素分布规律,稀有金属材料与工程,35(8),1315(2006)) |
| [8] | SUN Zhenyan,LIU Chunming,Diffusion and Phase Transformations in Alloys(Shenyang,Northeastern University Press,2002) p.39(孙振岩,刘春明,合金中的扩散与相变(沈阳,东北大学出版社,2002) p.39) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%