研究了Ti-60钛合金及Ti-48Al和Ti-48Al-12Cr(原子数分数,%)两种涂层在800℃的循环氧化行为.实验发现Ti-60钛合金基体在800℃氧化严重,氧化层发生了明显剥落.而两种涂层在800℃均能有效地保护Ti-60钛合金基体.在循环氧化过程中Ti-48Al-12Cr涂层增重明显小于Ti-48Al涂层,表现出更好的抗循环氧化能力.
参考文献
| [1] | I.Gurappa,Protection of titanium alloy components against high temperature corrosion,Materials Science and Engineering A,356(1-2),372(2003) |
| [2] | XIONG Yuming,ZHU Shenglong,Wang Fuhui,Effect of ultrafine emanel coating on the oxidation and mechanical property of Ti60 alloy,ACTA Metallurgica Sinica,40(7),768(2004)(熊玉明,朱圣龙,王福会,超细搪瓷涂层对Ti-60合金氧化及力学性能的影响,金属学报,40(7),768(2004)) |
| [3] | D.K.Das,Z.Alam,Cyclic oxidation behaviour of aluminide coatings on Ti-base alloy IMI-834 at 750 ℃,Surface & Coatings Technology,201(6),3406(2006) |
| [4] | C.Leyens,M.Peters,Titanium and Titanium Alloys (Beijing,Chemical Techonology Press,2005) p.190(C.莱茵斯,M.皮特尔斯,陈振华译,钛与钛合金 (北京,化学工业出版社,2005) p.190) |
| [5] | TANG Zhaolin,WANG Fuhui,WU Weitao,High temperature oxidation resistance of TiAlCr coatings for intermetallic TiAl,Journal of Chinese Society for Corrosion and Protection,18(1),35(1998)(唐兆麟,王福会,吴维(殳),TiAlCr涂层对TiAl金属间化合物抗高温氧化性能的影响,中国腐蚀与防护学报,18(1),35(1998)) |
| [6] | M.Fr(o)hlich,R.Braun,C.Leyens,Oxidation resistant coatings in combination with thermal barrier coatings on γ-TiAl alloys for high temperature applications,Surface & Coatings Technology,201(7),3911(2006) |
| [7] | G.S.Fox-Rabinovich,D.S.Wilkinson,S.C.Veldhuis,G.K.Dosbaeva,G.C.Weatherly,Oxidation resistant Ti-Al-Cr alloy for protective coating applications,Intermetallics,14,189(2006) |
| [8] | TANG Zhaolin,Protective coatings for TiAl intermetallic compound,PhD Thesis Institute of Metal Research,The Chinese Academy of Sciences(1996)(唐兆麟,钛铝金属间化合物的高温防护涂层,博士学位论文,中国科学院金属研究所,沈阳(1996)) |
| [9] | R.A.Perkins,K.T.Chiang,G.H.Meier,Formation of alumina on Ti-Al alloys,Scripta.Metallurgica,21(11),1505(1987) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%