研究了横向磁场对镍基高温合金DZ417G定向凝固显微组织的影响.在较低生长速率条件下,磁场显著影响合金的枝晶生长和宏观偏析.施加磁场后一次枝晶间距减小并在沿磁场方向试样的左侧出现了"斑状"偏析.随着生长速率的增加,磁场的影响减弱.从磁场在合金熔体中诱发热电磁对流,并影响枝晶生长的角度对实验结果进行了分析.
Some problems still exist in the directionally solidified superalloy, such as coarse dendritic structure, thick second phase and composition segregation. Many efforts have been made to enhance the overall performance of superalloy by improving the components and processes. How-ever, the higher alloying degree not only increases the solidification segregation, but also increases the tendency of precipitating σ-phases, Laves-phases, p-phases and other harmful phases. Therefore, it is crucial to improve the processes in order to enhance the performance of superalloy. It was known that the magnetic field effect is very obvious during the melt solidification process, which has been realized in the directional solidification of silicon, while the research on the magnetic field effect during the superalloy solidification process is few. So it is necessary to research the effect of magnetic field on directionally solidified superalloy. In this paper, the influence of horizontal magnetic field (≤0.8 T) on the microstructures of the superalloy D2417G during directional solidification was investigated. It was found that the magnetic field can induce the appearance of freckle-like macrosegregation and the decrease of the primary dendrite arm spacing at a low growing speed, however, with the increase of the growth speed, the effects become weak. Based on the thermoelectric magnetic convection (TEMC) in-duced by the magnetic field during solidification and the effect of the convection on the microstructure, the above experimental results were discussed and analyzed.
参考文献
| [1] | Matthiesen D H,Wargo M J,Motakef S,Carlson D J,Nakos J S,Witt A F.J Cryst Growth,1987; 85:557 |
| [2] | Robertson G D Jr,Oconner D J.J Cryst Growth,1986; 76:100 |
| [3] | Yang S,Liu W J.Mater Sci,2001; 36:5351 |
| [4] | Tewari S N,Shah R,Song H.Metall Mater Trans,1994; 25A:1535 |
| [5] | Li X,Fautrelle Y,Ren Z M.Acta Mater,2007; 55:3803 |
| [6] | Liu Z Y,Yang A M,Li J G,Shi Z X,Fu H Z.Mater Sci Prog,1992; 6:481(刘忠元,杨爱民,李建国,史正兴,傅恒志.材料科学进展,1992;6:481、 |
| [7] | Zhang N,Lin J P,Wang Y L,Chen G L.Aeronaut Mater,2006; 26:42(张宁,林均品,王艳丽,陈国良.航空材料学报,2006;26:42) |
| [8] | Ren W L,Zhang T,Ren Z M,Zhao A K,Zhong Y B,Guo J T.Mater Lett,2009; 63:382 |
| [9] | Utech H P,Flemings,M C.J Appl Phys,1966; 37:2021 |
| [10] | Alboussiere T,Moreau R,Camel D.C R Acad Sci,1991; 313:749 |
| [11] | Lehmann P,Moreau R,Camel D,Bolcato R.Acta Mater,1998; 46:4067 |
| [12] | Li X,Gagnoud A,Ren Z M,Fautrelle Y,Moreau R.Acta Mater,2009; 57:2180 |
| [13] | Moore J J,Shah N A.Met Rev,1983; 28:338 |
| [14] | Garandet J P,Alboussiere T.Prog Cryst Grorvth Charact Mater,1999; 38:100 |
| [15] | Lehmann P,Moreau R,Camel D,Bolcato R.J Cryst Growth,1998; 183:690 |
| [16] | Dupouy M D,Camel D,Favier J J.Acta Metall Mater,1992; 40:1791 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%