采用诱导型耦合等离子体辅助直流磁控溅射法在石英玻璃片上反应沉积TiO_2薄膜,通过X射线衍射(XRD),透射电子显微镜(TEM)和紫外可见光谱(UV-Vis)对薄膜特性进行表征.结果表明,叠加诱导型耦合等离子体和局部富氧增加了等离子体的反应活性,在金属溅射模式和低于200℃的沉积条件下,制备了高质量的锐钛矿相TiO_2薄膜;该薄膜在550 nm处的折射率和消光系数分别为2.51和7.8×10~(-4)
TiO_2thin films have been deposited on unheated glass substrates by an inductively coupled plasma (ICP) assisted direct current (dc) reactive magnetron sputtering. XRD, TEM and UV-Vis spectrophotometer have been used to characterize the films. It is shown that the addition of an ICP and the change of gas input strongly affect film growth and structure. High quality anatase phase TiO_2film has been prepared at the metallic mode of sputtering and at low deposition temperature by using the ICP assisted dc reactive magnetron sputtering and creating a gradient of oxygen favoring the oxidation of the growing film. This film is quite transparent in the visible region, and its refractive index n and the extinction coefficient K at 550 nm are 2.51 and 7.8×10~(-4), respectively.
参考文献
| [1] | Fujishima A,Honda K.Bull Chem Soc Jpn,1971; 44:1148 |
| [2] | Fujishima A,Honda K.Nature,1972; 238:37 |
| [3] | Kawai T,Sakata T.Nature,1980; 286:474 |
| [4] | Wang R,Hashimoto K,Fujishima A.Nature,1997; 388:431 |
| [5] | Lopez T,Gomez R,Pecci G.Mater Lett,1999; 40:59 |
| [6] | Kim J S,Joo H K,Lee T K.J Catal,2000; 194:484 |
| [7] | Szczyrbowski J,Brauer G,Ruske M,Bartella J,Schroeder J,Zmelty A.Surf Coat Technol 1999; 112:161 |
| [8] | Okimura K,Shibata A,Maeda N,Tashibana K,Nogushi Y,Tsuchida K.Jpn J Appl Phys,1995; 34:4950 |
| [9] | Baroch P,Musil J,Vlcek J,Nam K H,Han J G.Surf Coat Technol,2005; 193:107 |
| [10] | Heo C H,Lee S B,Boo J H.Thin Solid Films,2005; 475:183 |
| [11] | Kubart T,Depla D,Martin D M,Nyberg T,Berg S.Appl Phys Lett,2008; 92:221501 |
| [12] | Musil J,Herman D,Sichia J.J Vac Sci Technol 2006; 24A:521 |
| [13] | Toku H,Pessoa R S,Maciel H S,Massi M,Mengui U A.Surf Coat Technol,2008; 202:2126 |
| [14] | Zhang W,Li Y,Zhu S,Wang F.Surf Coat Technol,2004; 182:192 |
| [15] | Takamura K,Abe Y,Sasaki K.Vacuum,2004; 74:397 |
| [16] | Li Z G,Wu Y X,Miyake S.Surf Coat Technol,2009; 203:3661 |
| [17] | Li Z G,Miyake S,Mori M.Jpn J Appl Phys,2003; 42:7086 |
| [18] | Snyders R,Gouttebaron R,Dauchot J P,Hecq M.Surf Coat Technol,2005; 200:448 |
| [19] | Snyders R,Dauchot J P,Hecq M.Plasma Process Polym,2007; 4:113 |
| [20] | Boukrouh S,Bensaha R,Bourgeois S,Finot E,Marco de Lucas M C.Thin Solid Films,2008; 516:6353 |
| [21] | Miao L,Tanemura S,Kondo Y,Iwata M,Toh S,Kaneko K.Appl Surf Sci,2004; 238:125 |
| [22] | Shen Y,Yu H,Yao J,Shao S,Fan Z,He H,Shao J.Optics Laser Technol,2008; 40:550 |
| [23] | Dzibrou D,Grishin A M,Kawasaki H.Thin Solid Films,2008; 516:8697 |
| [24] | Kim S H,Hwangbo C K.Thin Solid Films,2008; 475:155 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%